PA6，LubriOne™ GF-1010 40 MS 2 HS Black 37对比PA6，RTP 207A HI物性表,价格行情_搜料

牌号信息	LubriOne™ GF-1010 40 MS 2 HS Black 37 物性表 PA6 & 美国普立万指导价格：暂无塑料库存：缺货	RTP 207A HI 物性表 PA6 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	Lubrione润滑和耐磨化合物被专门配制成自润滑材料，提供低摩擦系数和改进的耐磨性能。润滑油化合物已被证明可以减少摩擦、噪音、振动、热积聚并提高产品的耐久性。 LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。-每个RTP公司的初步产品数据- Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.-

产品描述
厂家：	美国普立万 Polyone	美国RTP
类别：	PA6 PA6	PA6 PA6
填料：
用途：	汽车领域的应用,消费品应用领域,滑轮,齿轮,商务设备,印刷机零件,家电部件,工业应用,传送机配件,轴承,滚轴
性能特点：	机械强度好,成核的,耐磨,热稳定性好 Good Rigidity,Nucleation,Good wear resistance,Heat Stabilized	冲击性能好,防火阻燃等级HB High impact resistance,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LubriOne™ GF-1010 40 MS 2 HS Black 37 RTP 207A HI 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL LubriOne™ GF-1010 40 MS 2 HS Black 37 RTP 207A HI 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

摩擦系数(与钢 - 动态)
friction coefficient ASTM D1894

摩擦系数(与钢 - 静态)
friction coefficient ASTM D1894

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT LubriOne™ GF-1010 40 MS 2 HS Black 37 RTP 207A HI 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃，6.4mm，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256-A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL LubriOne™ GF-1010 40 MS 2 HS Black 37 RTP 207A HI 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

电气性能
ELECTRICAL LubriOne™ GF-1010 40 MS 2 HS Black 37 RTP 207A HI 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

阻燃性能
FLAMMABILITY LubriOne™ GF-1010 40 MS 2 HS Black 37 RTP 207A HI 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

加工方式

注射 LubriOne™ GF-1010 40 MS 2 HS Black 37 RTP 207A HI 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

备注

1 一般属性：这些不能被视为规格。

2 类型 1, 0.20 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注