PA66，LNP™ THERMOCOMP™ RF007ES compound对比PA66，TAROMID A 280 G7 Y0物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ RF007ES compound 物性表 PA66 & 沙特沙伯基础指导价格：暂无塑料库存：缺货	TAROMID A 280 G7 Y0 物性表 PA66 & 意大利Taro Plast 指导价格：暂无塑料库存：缺货
牌号简介	LNP Thermocomp RF007ES是一种基于尼龙66树脂的化合物，含有35%的玻璃纤维。这种材料的附加特性包括：热稳定，易于成型。也称为：lnpThermocomp化合物rf-1007 em hs产品重新订购名称：rf007es LNP THERMOCOMP RF007ES is a compound based on Nylon 66 resin containing 35% Glass Fiber. Added features of this material include: Heat Stabilized, Easy Molding.	聚酰胺66中粘度35%玻璃纤维增强，热稳定，无卤阻燃剂UL94V0，流动性好，电气机械性能高，尺寸稳定性好。 Polyamide 66 medium viscosity 35% glass fibres reinforced, heat stabilized, halogen free flame retardant UL94 V0, good flow, high electrical and mechanical properties, good dimensional stability.

产品描述
厂家：	沙特沙伯基础 SABIC	意大利Taro Plast
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 35	玻璃纤维 35
用途：
性能特点：	易加工,热稳定性好 Excellent Processability,Heat Stabilized	尺寸稳定性好,电气性好,易流动,无卤,阻燃,热稳定性好,防火阻燃等级V-0 Good Dimensional Stability,Good Electrical Properties,Good liquidity,Halogen free,Flame Characteristics,Heat Stabilized,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位
UNIT 测试方法
TEST METHOD

Granule Humidity
Granule Humidity %

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³

收缩率(MD)
Shrinkage rate % 内部方法

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % 内部方法

收缩率(TD：24 hrs)
Shrinkage rate %

机械性能
MECHANICAL LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(--)
Dart impact equipped with measuring instruments J ISO 6603-2

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ ISO 11357-3

球压测试(230℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

连续使用温度(--)
Continuous use temperature ℃ IEC 60216

电气性能
ELECTRICAL LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位
UNIT 测试方法
TEST METHOD

相比漏电起痕指数
Compared to the leakage tracing index UL 746

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位
UNIT 测试方法
TEST METHOD

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(0.90 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

加工方式

注射 LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

注射速度 LNP™ THERMOCOMP™ RF007ES compound TAROMID A 280 G7 Y0 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 TARO 002

3 0.039 in/min

4 120°C/hr

5 20,000 hr

6 Short term


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
注射速度
备注
返回顶部

PA66，LNP™ THERMOCOMP™ RF007ES compound对比PA66，TAROMID A 280 G7 Y0对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别