PA66，Leona™ 14G15对比PA66，Ultramid® A3EG3物性表,价格行情_搜料

牌号信息	Leona™ 14G15 物性表 PA66 & 日本旭化成指导价格：30450.0元/吨塑料库存： 11500kg	Ultramid® A3EG3 物性表 PA66 & 德国巴斯夫指导价格：38640.0元/吨塑料库存： 19975kg
牌号简介	Leona™ 14G15是一种聚酰胺66（尼龙66）产品,含有的填充物为15% 玻璃纤维增强材料。它,在北美洲、非洲和中东、欧洲或亚太地区有供货。 Leona™ 14G15的应用领域包括汽车行业、电气/电子应用和工程/工业配件。特性包括: 阻燃/额定火焰高刚度高强度抗蠕变耐疲劳 Leona™ 14G15 is a Polyamide 66 (Nylon 66) product filled with 15% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Leona™ 14G15 include automotive, electrical/electronic applications and engineering/industrial parts. Characteristics include: Flame Rated Creep Resistant Fatigue Resistant Heat Resistant Heat Stabilizer	Ultramid® A3EG3是一种15%玻璃纤维增强注塑成型PA66级。典型应用包括中等硬度的机械部件和外壳，以及电绝缘部件。 Ultramid A3EG3 is a 15% glass fiber reinforced injection molding PA66 grade. Applications Typical applications include medium stiffness machinery components and housings, as well as electrically insulating parts.

产品描述
厂家：	日本旭化成 Asahi Kasei	德国巴斯夫 BASF
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 15	玻璃纤维 15
用途：	汽车的发动机罩下的零件,汽车领域的应用,电气/电子应用领域,构件	外壳,电气元件,电子绝缘,机器/机械部件
性能特点：	机械强度好,韧性好,耐疲劳性好,耐热性好,热稳定性好,防火阻燃等级HB Good Rigidity,Good flexibility,Fatigue resistance,Heat Resistance, Good,Heat Stabilized,HB	机械强度好,耐油 Good Rigidity,Grease resistance
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Leona™ 14G15 Ultramid® A3EG3 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % 内部方法

收缩率(TD)
Shrinkage rate % 内部方法

熔体质量流动速率()
Melt Flow Rate g/10min ISO 1133

冲击性能
IMPACT Leona™ 14G15 Ultramid® A3EG3 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Leona™ 14G15 Ultramid® A3EG3 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K DIN 52612

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数
Linear coefficient of thermal expansion

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

电气性能
ELECTRICAL Leona™ 14G15 Ultramid® A3EG3 单位
UNIT 测试方法
TEST METHOD

介电常数(23℃)
Dielectric constant 1 kHz IEC 60250

介电强度
Dielectric strength kV/mm ASTM D149

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻
Volumetric resistance Ω.cm IEC 60093

体积电阻率(23℃)
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数(3.00 mm)
Compared to the leakage tracing index V IEC 60112

绝缘强度()
Insulation strength KV/mm IEC 60243-1

耗散因数(23℃ )
Dissipation factor 1 MHz IEC 60250

耗散因数(相比漏电起痕指数)
Dissipation factor V IEC 60112

表面电阻率
Surface resistivity ohms ASTM D257

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Leona™ 14G15 Ultramid® A3EG3 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.75 mm)
Flame retardant level UL 94

阻燃等级(0.80mm)
Flame retardant level UL-94

阻燃等级(1.70mm)
Flame retardant level UL-94

阻燃等级(3.00mm)
Flame retardant level UL-94

机械性能
MECHANICAL Leona™ 14G15 Ultramid® A3EG3 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(23℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

拉伸蠕变模量(1000 Hr)
Tensile creep modulus MPa ISO 899-1

泰伯耐磨性(1000 周期)
Taber abraser mg ASTM D1044

洛氏硬度(M 级)
Rockwell hardness ASTM D785

洛氏硬度(M 级)
Rockwell hardness ISO 2039-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

加工方式

注射 Leona™ 14G15 Ultramid® A3EG3 单位测试方法

干燥时间 Hr

干燥温度 °C

水份含量 %

注塑温度模具温度 °C

注塑温度模头温度 °C

注塑温度螺筒中部温度 °C

注塑温度螺筒前部温度 °C

注塑温度螺筒后部温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
备注
返回顶部