PC+ABS，PULSE™ 2100LG对比PC+ABS，Iupilon® MB2215R物性表,价格行情_搜料

牌号信息	PULSE™ 2100LG 物性表 PC+ABS & 美国盛禧奥指导价格：暂无塑料库存：缺货	Iupilon® MB2215R 物性表 PC+ABS & 日本三菱指导价格：暂无塑料库存：缺货
牌号简介	PULSE™ 2100LG 工程树脂在需要高韧性的应用领域具有最好的性能表现，这些应用从单件物品到复杂零部件均有涉及。PULSE 2100LG 可以承受极高和极低的温度，在快速的、重复性的温度波动下，也有良好的性能表现。特点: 低光泽 -20°F 延展性性能范围宽优异可加工性批次稳定性耐化学性 PULSE™ 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can withstand high and low temperature extremes and rapid, repeated temperature fluctuations. Benefits: Low gloss appearance Low temperature ductility Wide range of performance Superior processability Lot to lot consistency Good chemical resistance	Iupilon® MB2215R是一种聚碳酸酯+丙烯腈丁二烯苯乙烯(PC+ABS)材料,。该产品在北美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Iupilon® MB2215R的主要特性有: 阻燃/额定火焰可焊 Iupilon® MB2215R is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® MB2215R are: Flame Rated Weldable

产品描述
厂家：	美国盛禧奥 Trinseo	日本三菱 Mitsubishi
类别：	PC+ABS PC+ABS	PC+ABS PC+ABS
填料：
用途：
性能特点：	易加工,机械强度好-延展,耐化学性,热稳定性好,低光泽 Excellent Processability,Ductility,Solvent resistance,Heat Stabilized,Low Gloss	焊接,防火阻燃等级HB Welding,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL PULSE™ 2100LG Iupilon® MB2215R 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183-2

密度
Density g/cm³ ISO 1183/B

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(230℃，3.8 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(250℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(260℃，3.80kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL PULSE™ 2100LG Iupilon® MB2215R 单位
UNIT 测试方法
TEST METHOD

Nominal strain at break
Nominal strain at break % ISO 527-2 2

弯曲强度
bending strength MPa ISO 178

弯曲强度(3.20 mm，注塑成型)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(3.20 mm，注塑成型)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(屈服)
Tensile strain % ISO 527-2 2

拉伸应变(屈服，3.20 mm，注塑成型)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，3.20 mm，注塑成型)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2 2

拉伸强度(屈服，3.20 mm，注塑成型)
tensile strength MPa ASTM D638

拉伸强度(断裂，3.20 mm，注塑成型)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量(3.20 mm，注塑成型)
Tensile modulus MPa ASTM D638

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2

冲击性能
IMPACT PULSE™ 2100LG Iupilon® MB2215R 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-30℃，3.2mm，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃，3.2mm，注塑成型)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁冲击强度(-30℃)
Charpy impact strength ISO 179/1eU 2

简支梁冲击强度(23℃)
Charpy impact strength ISO 179/1eU 2

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 2

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 2

装有测量仪表的落镖冲击(-29℃，3.20 mm，Peak Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，3.20 mm，Peak Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL PULSE™ 2100LG Iupilon® MB2215R 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa)
Hot deformation temperature ℃ ISO 75-2 2

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-2 2

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2 2

线性热膨胀系数(MD：-40~82℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 4

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/A120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306 2

光学性能
OPTICAL PULSE™ 2100LG Iupilon® MB2215R 单位
UNIT 测试方法
TEST METHOD

GMCP88(Light Stipple)
GMCP88（Light Stipple） % ASTM D542

Monticello
Monticello % ASTM D542

光泽度(60°，Smooth)
gloss ASTM D542

阻燃性能
FLAMMABILITY PULSE™ 2100LG Iupilon® MB2215R 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 PULSE™ 2100LG Iupilon® MB2215R 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 ??????,?? ISO 10350 ??? 23°C/50%r.h. ???

3 21,7 ft/sec

4 速率 A (50°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
光学性能
阻燃性能
加工方式
注射
备注
返回顶部