PPO(PPE)+PS+PP，DELOXEN P 3010对比PPO(PPE)+PS+PP，NORYL PPX™ PPX830 resin物性表,价格行情_搜料

牌号信息	DELOXEN P 3010 物性表 PPO(PPE)+PS+PP & 意大利Vamp 指导价格：暂无塑料库存：缺货	NORYL PPX™ PPX830 resin 物性表 PPO(PPE)+PS+PP & 沙特沙伯基础指导价格：暂无塑料库存： 10000kg
牌号简介	PPO/PP，30%玻璃纤维增强，不含阻燃剂，力学性能好。 PPO / PP, 30% glass fiber reinforced, not Flame Retardant compound, good mechanical properties.	noryl ppx ppx830树脂noryl ppx830聚苯氧化物（ppo）+聚丙烯（pp）树脂是一种30%玻璃增强注塑级树脂，HDT/1.8Mpa耐温153摄氏度，拉伸模量7600兆帕；该等级已开发用于尺寸稳定性、耐温性和耐化学性能够D是必需的。Noryl PPX830是一种不透明材料，仅限有限颜色。 NORYL PPX™ PPX830 resin NORYL PPX830 Polyphenylene Oxide (PPO) + Polypropylene (PP) resin is a 30 % Glass Reinforced, injection moldable grade with a HDT /1.8MPa temperature resistance of 153 deg C and a Tensile modulus of 7600 MPa; this grade has been developed for application where dimension stability, temperature and chemical resistance could be required. NORYL PPX830 is an opaque material available in limited colors only.

产品描述
厂家：	意大利Vamp	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS+PP PPO(PPE)+PS+PP	PPO(PPE)+PS+PP PPO(PPE)+PS+PP
填料：	玻璃纤维 30	玻璃纤维 30
用途：
性能特点：		尺寸稳定性好,耐化学性,防火阻燃等级HB Good Dimensional Stability,Solvent resistance,HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL DELOXEN P 3010 NORYL PPX™ PPX830 resin 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL DELOXEN P 3010 NORYL PPX™ PPX830 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT DELOXEN P 3010 NORYL PPX™ PPX830 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180/A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

装有测量仪表的落镖冲击(-30℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL DELOXEN P 3010 NORYL PPX™ PPX830 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-30~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：-40~95℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-30~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~95℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

阻燃性能
FLAMMABILITY DELOXEN P 3010 NORYL PPX™ PPX830 resin 单位
UNIT 测试方法
TEST METHOD

1.00 mm
1.00 mm UL 94

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

加工方式

注射 DELOXEN P 3010 NORYL PPX™ PPX830 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部