PC，LNP™ THERMOCOMP™ DX13354X compound对比PC，LNP™ THERMOCOMP™ D151 compound物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ DX13354X compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LNP™ THERMOCOMP™ D151 compound 物性表 PC & 沙特沙伯基础指导价格：106864.27元/吨塑料库存： 1000kg
牌号简介	LNPThermocomp化合物DX13354X是一种可着色、玻璃纤维增强的聚碳酸酯树脂基材料溶液，具有稳定的电镀和射频性能，具有优异的刚度、良好的表面和良好的冲击强度。该产品可用于激光直接结构应用的内部和外部零件。 LNP* Thermocomp* compound DX13354X is a colorable, glass fiber reinforced Polycarbonate resin based LDS material solution with stable plating and RF performance, providing excellent stiffness with good surface and good impact strength. The product is available for internal and external parts for Laser Direct Structuring applications.	LNPThermocompD151（实验级名称为extc8274）是一种基于聚碳酸酯树脂的化合物，含有玻璃纤维、阻燃剂。该材料的附加特性包括：高模量、表面良好、平整度好、延展性好、无溴无氯阻燃。 LNP* Thermocomp* D151 (experimental grade name as EXTC8274) is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good surface, good flatness, good ductility, Non-Brominated & Non-Chlorinated Flame Retardant.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	玻璃纤维	玻璃纤维
用途：	激光直接成型
性能特点：	机械强度好,表面光泽度好,冲击性能好 Good Rigidity,Good surface appearance,High impact resistance	表面光泽度好,机械强度好-延展,无卤,阻燃,防火阻燃等级V-2,防火阻燃等级V-1,防火阻燃等级V-0 Good surface appearance,Ductility,Halogen free,Flame Characteristics,V-2,V-1,V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ DX13354X compound LNP™ THERMOCOMP™ D151 compound 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ASTM D1238

熔体体积流动速率(300℃，2.16 kg)
Melt Volume Rate cm³/10min

熔体质量流动速率(280℃，2.16kg)
Melt Flow Rate g/10min

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min

熔体质量流动速率(300℃，2.16kg)
Melt Flow Rate g/10min

机械性能
MECHANICAL LNP™ THERMOCOMP™ DX13354X compound LNP™ THERMOCOMP™ D151 compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790，ISO 178

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ THERMOCOMP™ DX13354X compound LNP™ THERMOCOMP™ D151 compound 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/2U

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/2C

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ DX13354X compound LNP™ THERMOCOMP™ D151 compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃

电气性能
ELECTRICAL LNP™ THERMOCOMP™ DX13354X compound LNP™ THERMOCOMP™ D151 compound 单位
UNIT 测试方法
TEST METHOD

介电常数(1.10 GHz)
Dielectric constant

介电常数(1.9 GHz)
Dielectric constant

介电常数(10.0 GHz)
Dielectric constant

介电常数(5.00 GHz)
Dielectric constant

耗散因数(1.1 GHz)
Dissipation factor

耗散因数(1.9 GHz)
Dissipation factor

耗散因数(10 GHz)
Dissipation factor

耗散因数(5 GHz)
Dissipation factor

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ DX13354X compound LNP™ THERMOCOMP™ D151 compound 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.30 mm)
Flame retardant level

阻燃等级(0.40 mm)
Flame retardant level

阻燃等级(0.60 mm)
Flame retardant level

加工方式

注射 LNP™ THERMOCOMP™ DX13354X compound LNP™ THERMOCOMP™ D151 compound 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 80*10*4

5 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 0.079 in/min

6 Break

7 80*10*4 sp=62mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部