ABS，Terluran® GP-25对比ABS，CYCOLAC™ FXS610SK resin物性表,价格行情_搜料

牌号信息	Terluran® GP-25 物性表 ABS & 瑞士英力士苯领指导价格：暂无塑料库存：缺货	CYCOLAC™ FXS610SK resin 物性表 ABS & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Terluran® GP-25是一种易于流动的通用注塑级产品，具有高抗冲击性和热变形性；适用于广泛的应用领域，尤其是在外壳领域。具有优异的着色性、中等流动性、良好的抗冲击性、良好的热变形性、高质量的表面光洁度和光泽应用注塑成型器具外壳、家用和卫生器具、玩具、汽车零部件。 Terluran® GP-25 is an easy-flow, general purpose injection molding grade with high resistance to impact and heat distortion; intended for a wide range of applications, particularly in the housings sector. FEATURES Excellent colorability Medium flow Good impact resistance Good heat distortion resistance High quality surface finish and gloss APPLICATIONS Injection molding Appliance housings Household and sanitary appliances Toys Automotive components	Innoplus HD4200B是高密度聚乙烯吹塑级产品，具有刚性高、外观好、加工性好等特点。适用于高生产率或高速吹塑机。典型应用：食品包装、奶瓶、个人护理容器 CYCOLAC FXS610SK is a multi purpose ABS injection moulding grade, providing a favourable balance of engineering properties. CYCOLAC FXS610SK is suitable for those applications that require sparkle colour effects.

产品描述
厂家：	瑞士英力士苯领 INEOS	沙特沙伯基础 SABIC
类别：	ABS ABS	ABS ABS
填料：
用途：	卫浴产品,玩具,家用货品,电器用具,外壳,汽车领域的应用	食品包装,个人护理,容器,瓶子
性能特点：	表面光泽度好,冲击性能好,流动性中等,着色性好 Good surface appearance,High impact resistance,Moderate liquidity,Good coloring	机械强度好,易加工,表面光泽度好,食品接触,高密度,防火阻燃等级HB Good Rigidity,Excellent Processability,Good surface appearance,Food contact compliance,High density,HB
加工条件：	注射成型 Injection Molding	吹塑成型

技术参数

物理性能
PHYSICAL Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % 内部方法

收缩率(MD：2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD：2.0 mm)
Shrinkage rate % ISO 294-4

熔体体积流动速率(220℃，10 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

泰伯耐磨性(1000 周期，1000 g，CS-17 转轮)
Taber abraser mg 内部方法

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

光学性能
OPTICAL Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位
UNIT 测试方法
TEST METHOD

黄度指数
Yellowness index YI DIN6167

热性能
THERMAL Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K DIN 52612

导热系数
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

熔融温度
Melting temperature ℃ ISO 11357-3

球压测试(75℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~60℃)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(TD：23~60℃)
Linear coefficient of thermal expansion 1/℃

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306/A50

电气性能
ELECTRICAL Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位
UNIT 测试方法
TEST METHOD

介电强度(0.8 mm，在油中)
Dielectric strength kV/mm

介电强度(1.6 mm，在油中)
Dielectric strength kV/mm

介电强度(3.2 mm，在油中)
Dielectric strength kV/mm

体积电阻
Volumetric resistance Ω.cm IEC 60093

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率(1 MHz)
Relative permittivity

相对电容率(50 Hz)
Relative permittivity

相对电容率(60 Hz)
Relative permittivity

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor

耗散因数(50 Hz)
Dissipation factor

耗散因数(60 Hz)
Dissipation factor

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位
UNIT 测试方法
TEST METHOD

All color
All color HB UL-94

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(1.50 mm)
Flame retardant level UL 94

冲击性能
IMPACT Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m²

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

加工方式

注射 Terluran® GP-25 CYCOLAC™ FXS610SK resin 单位测试方法

加工熔体温度 °C

喷嘴温度 °C

射嘴温度 °C

干燥时间 Hr

干燥时间 hr

干燥温度 °C

建议水份含量 %

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 4h/80°C

1 一般属性：这些不能被视为规格。

2 Partial break

3 速率 A (50°C/h), 压力1 (10N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
光学性能
热性能
电气性能
阻燃性能
冲击性能
加工方式
注射
备注