HDPE，Marlex® HHM 5502LD对比HDPE，Network Polymers HDPE 50 0355物性表,价格行情_搜料

牌号信息	Marlex® HHM 5502LD 物性表 HDPE & 沙特Saudi 指导价格：暂无塑料库存：缺货	Network Polymers HDPE 50 0355 物性表 HDPE & 美国Network 指导价格：暂无塑料库存：缺货
牌号简介	Marlex® HHM 5502LD是一种高密度聚乙烯材料,。该产品在北美洲或拉丁美洲有供货,加工方式为:吹塑成型或注吹成型。 Marlex® HHM 5502LD的主要特性有: 高分子量环保/绿色己烯共聚单体加工性能良好抗静电典型应用领域包括: 家庭应用容器食品接触应用 This high molecular weight, ethylene-hexene copolymer with antistatic agent is tailored for lightweight blow molded containers that require: Excellent stiffness Exceptional processability Durability Recyclability Typical blow molded applications for HHM 5502LD include: Detergent bottles Household and industrial chemical containers This resin meets these specifications: ASTM D4976 - PE 235 FDA 21 CFR 177.1520(c) 3.1a, for use in molded containers, foods with pH>5 of types I, IV-B, VI-B, VII-B and VIII per Table 1 of 21 CFR 176.170(c) and conditions of use E through G per Table 2 of 21 CFR 176.170(c) Listed in the Drug Master File	Network Polymers HDPE 50 0355是一种高密度聚乙烯产品,。它可以通过吹塑成型或挤出进行加工,在北美洲有供货。 Network Polymers HDPE 50 0355 is a High Density Polyethylene product. It can be processed by blow molding or extrusion and is available in North America.

产品描述
厂家：	沙特Saudi	美国Network
类别：	HDPE HDPE	HDPE HDPE
填料：
用途：	吹制容器,家用货品
性能特点：	机械强度好,易加工,可回收,高分子量,经久耐用,抗静电,己烯共聚单体 Good Rigidity,Excellent Processability,Renewable resources,High molecular weight,Durability,Antistatic property,Hexene copolymers
加工条件：	注吹成型	吹塑成型

技术参数

物理性能
PHYSICAL Marlex® HHM 5502LD Network Polymers HDPE 50 0355 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

抗环境应力开裂
ESCR(Environmental Stress Cracking Resistance) hr

抗环境应力开裂
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

抗环境应力开裂(F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693A

抗环境应力开裂(F50)
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693B

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率()
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL Marlex® HHM 5502LD Network Polymers HDPE 50 0355 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790B

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

热性能
THERMAL Marlex® HHM 5502LD Network Polymers HDPE 50 0355 单位
UNIT 测试方法
TEST METHOD

加工温度
Processing temperature ℃

线性热膨胀系数
Linear coefficient of thermal expansion

脆化温度
Embrittlement temperature ℃ ASTM D746

备注

1 for use in molded containers, conditions E through G, foods with pH>5 of types I, IV-B, VI-B, VII-B and VIII, per 21 CFR 176.170(c), Tables 1 & 2

2 一般属性：这些不能被视为规格。

3 类型 4, 2.0 in/min

4 0.50 in/min

1 一般属性：这些不能被视为规格。

2 程序 A

3 2.0 in/min

4 方法 I (三点负荷), 0.050 in/min