牌号信息	Novodur® 377 物性表 ABS & 瑞士英力士苯领指导价格：暂无塑料库存：缺货	Sindustris ABS LMP322 物性表 ABS & 澳大利亚Sincerity 指导价格：暂无塑料库存：缺货
牌号简介	Novodur® 377是一种注射成型级的ABS，具有标准冲击强度，高流动性和高光泽的电镀应用。特点：标准冲击强度、高流动性、易流动性、家用电器、电子产品、通用注塑、玩具、运动休闲 Novodur® 377 is an injection molding grade of ABS with standard impact strength, high flow and high gloss for electroplating application. FEATURES Standard impact strength High flow Easy flowing APPLICATIONS Home appliances Electrical and electronics General Injection Molding Application Toys, Sport & Leisure	Sindustris ABS LMP322是一种丙烯腈丁二烯苯乙烯(ABS)材料,。该产品在亚太地区有供货,加工方式为:注射成型。 Sindustris ABS LMP322的主要特性为:阻燃/额定火焰。典型应用领域包括: 电气用具手柄装饰部件 Sindustris ABS LMP322 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Primary attribute of Sindustris ABS LMP322: Flame Rated. Typical applications include: Appliances Decorative Parts Handles

产品描述
厂家：	瑞士英力士苯领 INEOS	澳大利亚Sincerity
类别：	ABS ABS	ABS ABS
填料：
用途：	玩具,电气/电子应用领域,电器用具,通用,体育用品	电器用具,装饰部件,把手
性能特点：	表面光泽度好,流动性高 Good surface appearance,High liquidity	易流动,电镀,防火阻燃等级HB Good liquidity,Electroplating,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Novodur® 377 Sindustris ABS LMP322 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

光学性能
OPTICAL Novodur® 377 Sindustris ABS LMP322 单位
UNIT 测试方法
TEST METHOD

光泽度
gloss % ISO 2813

热性能
THERMAL Novodur® 377 Sindustris ABS LMP322 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，6.4 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/Af

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 5

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/A50

阻燃性能
FLAMMABILITY Novodur® 377 Sindustris ABS LMP322 单位
UNIT 测试方法
TEST METHOD

阻燃等级
Flame retardant level UL 94

阻燃等级(1.50mm)
Flame retardant level UL-94

阻燃等级(3.00mm)
Flame retardant level UL-94

冲击性能
IMPACT Novodur® 377 Sindustris ABS LMP322 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-30℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，6.4mm)
Impact strength of cantilever beam notch J/m ASTM D256

机械性能
MECHANICAL Novodur® 377 Sindustris ABS LMP322 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(3.20 mm)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(3.20 mm)
Bending modulus MPa ASTM D790

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸强度(屈服，23 ℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，3.20 mm)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

拉伸模量(3.20 mm)
Tensile modulus MPa ASTM D638

洛氏硬度
Rockwell hardness R 级 ISO 2039-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

注射 Novodur® 377 Sindustris ABS LMP322 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 4h/80°C

3 标准 B (120°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 0.039 in/min

3 2.0 in/min

4 0.59 in/min

5 速率 A (50°C/h), 载荷2 (50N)