PP均聚，Petroquim PP PH 1310对比PP均聚，Moplen HP2619A物性表,价格行情_搜料

牌号信息	Petroquim PP PH 1310 物性表 PP均聚 & 智利Petroquim 指导价格：暂无塑料库存：缺货	Moplen HP2619A 物性表 PP均聚 & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货
牌号简介	适用于注塑成型，易加工，加工过程稳定性好，刚性好，力学性能平衡。建议用于制造中等壁厚的一般零件。用途：家用物品，厨房用具，食品罐和托盘，盖子和玩具。 Apt for injection molding, easily processable, good stability during the process, good stiffness and balance of mechanical properties. Recommended for use in fabricating general parts with a medium wall thickness. Applications: Household items, kitchen utensils, food jars and trays, lids and toys.	Moplen HP2619A适用于挤压应用。它是由一个防气体褪色稳定包装制定的。Moplen HP2619A设计用于生产细旦短纤维。典型的应用是热粘合非织造布。有关监管信息，请参阅Moplen HP2619A产品管理公告（PSB）。 Moplen HP2619A is suitable for extrusion applications. It is formulated with an anti-gasfading stabilisation package. Moplen HP2619A is designed for the production of fine denier staple fibres. Typical application is thermal-bonded nonwovens. For regulatory information please refer to Moplen HP2619A Product Stewardship Bulletin (PSB).

产品描述
厂家：	智利Petroquim Petroquim	荷兰利安德巴塞尔 LyondellBasell
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	通用,玩具,食品容器,护罩,盖子,家用货品	线,纺粘无纺布,短纤维,细丝
性能特点：	机械强度好,易加工,均聚物 Good Rigidity,Excellent Processability,Homopolymer	均聚物 Homopolymer
加工条件：	注射成型 Injection Molding	Continuous Filament/Spinning

技术参数

物理性能
PHYSICAL Petroquim PP PH 1310 Moplen HP2619A 单位
UNIT 测试方法
TEST METHOD

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Petroquim PP PH 1310 Moplen HP2619A 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

冲击性能
IMPACT Petroquim PP PH 1310 Moplen HP2619A 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Petroquim PP PH 1310 Moplen HP2619A 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

加工方式

注射 Petroquim PP PH 1310 Moplen HP2619A 单位测试方法

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 压力1 (10N)

1 一般属性：这些不能被视为规格。