POM共聚，Ultraform® W 2320 003 UNC Q600对比POM共聚，Hostaform® C 27021 XAP C物性表,价格行情_搜料

牌号信息	Ultraform® W 2320 003 UNC Q600 物性表 POM共聚 & 德国巴斯夫指导价格：暂无塑料库存：缺货	Hostaform® C 27021 XAP C 物性表 POM共聚 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货
牌号简介	Ultraform® W 2320 003 UNC Q600是一种非常容易流动和快速凝固的注塑POM级产品，用于加工非常困难但机械性能较低的场合。含有脱模剂。典型应用包括薄壁零件。 Ultraform W 2320 003 UNC Q600 is a very easy flowing and rapidly solidifying injection molding POM grade for use where processing is extremely difficult but mechanical properties are lower. Contains a mold release agent. Applications Typical applications include thin walled parts.	POM共聚物易流动注射成型等级，排放量和迁移率极低；根据VDA 275<2 mg/kg（天然等级）设计用于消费包装排放。根据21 CFR 177.2470 FDA=食品和药品管理局（美国），单体和添加剂符合欧盟法规（欧盟）10/2011 FDA。 POM copolymer Easy flow injection molding grade with very low emissions and migrations; designed for consumer packaging. Emission according to VDA 275 < 2 mg/kg (natural grades) Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 FDA = Food and Drug Administration (USA)

产品描述
厂家：	德国巴斯夫 BASF	美国塞拉尼斯 Celanese
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：
用途：	薄壁部件	包装
性能特点：	易流动,含脱模剂,共聚物,防火阻燃等级HB Good liquidity,Good stripping performance,Copolymer,HB	易流动,低VOC,低移位,防火阻燃等级HB Good liquidity,Low odor,Low to no mobility,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultraform® W 2320 003 UNC Q600 Hostaform® C 27021 XAP C 单位
UNIT 测试方法
TEST METHOD

Melt Specific Heat
Melt Specific Heat J/kg/℃ Internal Method

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，50% RH)
Water absorption rate % ASTM D570

吸水率(饱和)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % ISO 294-4

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体密度
Melt density g/cm³ Internal Method

熔体导热性
Melt thermal conductivity W/m/K Internal Method

顶出温度
Ejection temperature ℃ Internal Method

机械性能
MECHANICAL Ultraform® W 2320 003 UNC Q600 Hostaform® C 27021 XAP C 单位
UNIT 测试方法
TEST METHOD

Tensile Creep Modulus(1 hr)
Tensile Creep Modulus（1 hr） MPa ISO 899-1

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸应变(屈服，23℃)
Tensile strain % ASTM D638

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/50

拉伸强度(屈服，-40℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，80℃)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

拉伸蠕变模量(1000 hr)
Tensile creep modulus MPa ISO 899-1

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2/1A/50

标称拉伸断裂应变(23℃)
Nominal tensile fracture strain % ISO 527-2

冲击性能
IMPACT Ultraform® W 2320 003 UNC Q600 Hostaform® C 27021 XAP C 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ultraform® W 2320 003 UNC Q600 Hostaform® C 27021 XAP C 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度
Melting temperature ℃ ISO 11357-3

熔融温度(DSC)
Melting temperature ℃ ISO 3146

相对温度指数(1.5 mm)
Relative temperature index ℃ UL 746

相对温度指数(3.0 mm)
Relative temperature index ℃ UL 746

相对温度指数(冲击机械性能)
Relative temperature index UL 746

相对温度指数(强度机械性能)
Relative temperature index UL 746

相对温度指数(电气性能)
Relative temperature index UL 746

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Ultraform® W 2320 003 UNC Q600 Hostaform® C 27021 XAP C 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant IEC 60250

介电常数(100 Hz)
Dielectric constant IEC 60250

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

体积电阻率(1.50 mm)
Volume resistivity ohms·cm ASTM D257

相对电容率(1 MHz)
Relative permittivity IEC 60250

相对电容率(100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms ASTM D257

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Ultraform® W 2320 003 UNC Q600 Hostaform® C 27021 XAP C 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(3.00 mm)
Flame retardant level UL 94

加工方式

注射 Ultraform® W 2320 003 UNC Q600 Hostaform® C 27021 XAP C 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

螺杆长径比

备注

1 一般属性：这些不能被视为规格。

2 1.5 mm

1 一般属性：这些不能被视为规格。

2 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注