牌号信息	TOTAL Polypropylene PPC 4280W 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货	TOTAL Polypropylene PPC 3640 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	全石油化工聚丙烯4280W是一种低熔融流量为1.3g/10min的抗冲击共聚物。4280W聚丙烯具有低流动性，提供了具有优异抗冲击性能的熔融强度。它是为了增加硬度和表面硬度而成核的。4280W特别适用于型材和板材挤压、挤压热成型和重型注塑成型应用。 Total Petrochemicals Polypropylene 4280W is an impact copolymer with a low Melt Flow of 1.3 g/10min. 4280W polypropylene has a low fluidity providing melt strength with excellent impact properties. It is nucleated for added stiffness and surface hardness. 4280W is designed to be particularly suited for profile and sheet extrusion, extrusion-thermoforming and heavy-duty injection molded applications.	聚丙烯PPC 3640是一种有核异相共聚物，其熔体流动指数为1.3 g/10 min。聚丙烯PPC 3640具有提高的刚度、抗蠕变和高抗冲击性。聚丙烯PPC 3640是专门为波纹纸板、波纹管和双壁管、导管和其他挤压应用而开发的。 Polypropylene PPC 3640 is a nucleated heterophasic copolymer with a Melt Flow Index of 1.3 g/10 min. Polypropylene PPC 3640 is characterized by improved stiffness, creep resistance and high impact resistance. Polypropylene PPC 3640 has been developed specifically for the extrusion of corrugated cardboard, corrugated and twin walled pipes, conduit pipe and other extrusion applications.

产品描述
厂家：	法国道达尔 TOTAL	法国道达尔 TOTAL
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	片材,型材,热成型应用	管道系统,波纹管
性能特点：	机械强度好,流动性低,冲击性能好,硬度高,成核的,熔体强度好,抗冲共聚物 Good Rigidity,Low liquidity,High impact resistance,Good Hardness,Nucleation,Good melt strength,Impact copolymer	机械强度好,韧性好,冲击性能好,成核的,抗冲共聚物 Good Rigidity,Good flexibility,High impact resistance,Nucleation,Impact copolymer
加工条件：	热成型 Thermo forming	管路挤出成型

技术参数

物理性能
PHYSICAL TOTAL Polypropylene PPC 4280W TOTAL Polypropylene PPC 3640 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

密度
Density g/cm³ ISO 1183

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 1183

机械性能
MECHANICAL TOTAL Polypropylene PPC 4280W TOTAL Polypropylene PPC 3640 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT TOTAL Polypropylene PPC 4280W TOTAL Polypropylene PPC 3640 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch J/m

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL TOTAL Polypropylene PPC 4280W TOTAL Polypropylene PPC 3640 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ 内部方法

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
备注