3D打印材料，DuraForm® HST对比3D打印材料，ProtoTherm 12110物性表,价格行情_搜料

牌号信息	DuraForm® HST 物性表 3D打印材料 & 美国3D Systems 指导价格：暂无塑料库存：缺货	ProtoTherm 12110 物性表 3D打印材料 & 帝斯曼指导价格：暂无塑料库存：缺货
牌号简介	应用功能原型和最终用途零件需要高刚度和/或高耐热性典型应用包括：无人机结构部件外壳和外壳叶轮连接器消费体育用品具有高比刚度、耐高温、各向异性机械性能，就像纤维填充，注塑成型材料，非导电和射频透明，易于表面处理，功能性原型可以在“现实生活”环境中进行测试。复杂的最终用途零件可以经济地在低到中等体积中制造，在高温下具有吸引力的表面处理的承重应用中表现出色。 Applications Functional prototypes and end-use parts that require high stiffness and/or elevated thermal resistance Typical Applications include: UAV structural components Housings and enclosures Impellers Connectors Consumer sporting goods Features High specific stiffness Elevated temperature resistance Anisotropic mechanical properties just like fiber-filled, injection molded materials Non-conductive and RF transparent Easy-to-finish surface Benefits Functional prototypes can be tested in "real life" environments Complex end-use parts can be economically manufactured in low-to-medium volumes Excels in load-bearing applications at higher temperatures Attractive surface finish	DSM的SomosProtoTherm 12110是一种液态光聚合物，能够生产出坚固、耐高温、防水的部件。用Somos ProtoTherm 12110制造的零件具有樱桃红外观，经过热处理后变成橘红色。应用somos ProtoTherm 12110通过提高拉伸强度和在热处理后保持适当的断裂延伸率，使其与其他高温立体光刻材料有所不同。这使得这种材料非常适合在汽车和航空航天市场上的许多应用，在这些市场上需要能够抵抗高温的坚固部件。 DSM's Somos® ProtoTherm 12110 is a liquid photopolymer that produces strong, high-temperature tolerant, water-resistant parts. Parts created with Somos® ProtoTherm 12110 have a cherry-red appearance which turns to an orange-red color after thermal treatment. Applications Somos® ProtoTherm 12110 differentiates itself from other high temperature stereolithography materials by increasing in tensile strength and maintaining decent elongation at break after thermal treatment. This makes the material ideal for many applications in the automotive and aerospace markets where strong parts that can resist high temperatures are needed.

产品描述
厂家：	美国3D Systems	帝斯曼 DSM
类别：	3D打印材料 3D打印材料	3D打印材料 3D打印材料
填料：
用途：	成型,连接器,消费品应用领域,外壳,体育用品,构件	航空航天应用,成型,汽车领域的应用
性能特点：	机械强度好,表面光泽度好,阻燃,耐高温,防火阻燃等级HB Good Rigidity,Good surface appearance,Flame Characteristics,High Heat Resistance,HB	机械强度好,吸水率低,耐高温,防潮,拉伸性能好 Good Rigidity,Low or no water absorption,High Heat Resistance,Moisture resistance,Good Tensile Strength
加工条件：	3D Printing, Laser Sintering/Melting 3D Printing, Laser Sintering/Melting	立体光刻

技术参数

物理性能
PHYSICAL DuraForm® HST ProtoTherm 12110 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡)
Water absorption rate % ASTM D570

密度
Density g/cm³

密度
Density g/cm³ ASTM D792

粘度(30℃)
viscosity Pa·s

冲击性能
IMPACT DuraForm® HST ProtoTherm 12110 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m ASTM D256-A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

落锤冲击
Drop hammer impact J ASTM D5420

热性能
THERMAL DuraForm® HST ProtoTherm 12110 单位
UNIT 测试方法
TEST METHOD

比热
specific heat J/kg/℃ ASTM E1269

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

玻璃化转变温度
Glass transition temperature ℃ ASTM E1545

线性热膨胀系数(-40 到 0℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(0 到 50℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(100 到 150℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(50 到 100℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(MD)
Linear coefficient of thermal expansion ASTM E831

线性热膨胀系数(MD：0~50℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：85~145℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：0~50℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：85~145℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

电气性能
ELECTRICAL DuraForm® HST ProtoTherm 12110 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant ASTM D150

介电常数(1 MHz)
Dielectric constant ASTM D150

介电常数(60 Hz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耗散因数(1 kHz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY DuraForm® HST ProtoTherm 12110 单位
UNIT 测试方法
TEST METHOD

3.00 mm
3.00 mm UL 94

机械性能
MECHANICAL DuraForm® HST ProtoTherm 12110 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(断裂)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ASTM D2240

补充信息
DuraForm® HST ProtoTherm 12110 单位
UNIT 测试方法
TEST METHOD

Critical Exposure
Critical Exposure mJ/cm²

渗透深度
Penetration depth µm

备注

1 一般属性：这些不能被视为规格。

2 Z direction

3 X direction

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
补充信息
加工方式
备注