LDPE，Lupolen 1800 S对比LDPE，PETLIN LD M022X物性表,价格行情_搜料

牌号信息	Lupolen 1800 S 物性表 LDPE & 荷兰利安德巴塞尔指导价格：暂无塑料库存：缺货	PETLIN LD M022X 物性表 LDPE & 马来西亚PETLIN 指导价格：暂无塑料库存：缺货
牌号简介	Lupolen 1800 S是一种低密度聚乙烯（LDPE）树脂，用于注塑成型等加工方法。流动性好，柔软性、韧性和尺寸稳定性好。Lupolen 1800 S以颗粒形式交付，未添加。Lupolen 1800 S用于玩具、瓶盖和瓶盖、工程零件、运动和休闲设备等应用。Lupolen 1800 S不适用于医疗和制药应用。 Lupolen 1800 S is a low density polyethylene (LDPE) resin used in injection molding and other processing methods. It exhibits high flowability, and good softness, toughness and dimensional stability. Lupolen 1800 S is delivered in pellet form and is not additivated. Lupolen 1800 S is used in applications such as toys, caps & closures, engineering parts, and sports and leisure equipment. Lupolen 1800 S is not intended for use in medical and pharmaceutical applications.	PETLIN LD M022X是一种低密度聚乙烯树脂，主要用于注塑成型和母料应用。采用最先进的洁净管式反应器生产技术生产。 PETLIN LD M022X is a low density polyethylene resin designed primarily for injection molding and masterbatch applications. It is produced by the state-of-the-art Clean Tubular Reactor production technology.

产品描述
厂家：	荷兰利安德巴塞尔 LyondellBasell	马来西亚PETLIN
类别：	LDPE LDPE	LDPE LDPE
填料：
用途：	外壳,体育用品,玩具,复合,工程配件,护罩	盖子,家用货品,母料
性能特点：	易加工,韧性好,尺寸稳定性好,流动性高,成型周期快,低密度,柔软性好,耐低温冲击 Excellent Processability,Good flexibility,Good Dimensional Stability,High liquidity,Quick molding cycle,Low density,Soft,low-temperature impact resistance	表面光泽度好,低速凝固晶点,食品接触 Good surface appearance,Low speed solidification point,Food contact compliance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Lupolen 1800 S PETLIN LD M022X 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

抗环境应力开裂
ESCR(Environmental Stress Cracking Resistance) hr ASTM D1693

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

螺旋流动长度
Spiral flow length cm 内部方法

热性能
THERMAL Lupolen 1800 S PETLIN LD M022X 单位
UNIT 测试方法
TEST METHOD

熔融温度(DSC)
Melting temperature ℃ DIN 53765

熔融温度(DSC)
Melting temperature ℃ ISO 3146

结晶峰温(DSC)
Crystallization peak temperature ℃ DIN 53765

维卡软化温度
Vicat Softening Temp ℃ ISO 306

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

融合热量
Fusion heat J/g DIN 53765

机械性能
MECHANICAL Lupolen 1800 S PETLIN LD M022X 单位
UNIT 测试方法
TEST METHOD

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

球压硬度
Ball hardness MPa ISO 2039-1

邵氏硬度(邵氏 D)
Shore hardness ISO 868

加工方式

注射 Lupolen 1800 S PETLIN LD M022X 单位测试方法

加工熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 熔体温度: 356°F, 注塑压力: 1.45E+4 psi

3 2 mm

4 Tested in 10% nonionic surfactants

1 一般属性：这些不能被视为规格。