PS，PRE-ELEC® PS 1328对比PS，PRE-ELEC® PS 1326物性表,价格行情_搜料

牌号信息	PRE-ELEC® PS 1328 物性表 PS & 芬兰普宓斯指导价格：暂无塑料库存：缺货	PRE-ELEC® PS 1326 物性表 PS & 芬兰普宓斯指导价格：暂无塑料库存：缺货
牌号简介	PRE-ELEC® PS 1328是一种基于聚苯乙烯的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® PS 1328具有优良的机械性能，易于挤出或注塑成型。典型的应用包括注射成型手提箱和静电放电敏感产品的盒子。 PRE-ELEC® PS 1328 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PS 1328 has excellent mechanical properties and is easy to extrude or injection mould. Typical applications include injection moulded tote bins and boxes for ESD sensitive products.	PRE-ELEC® PS 1326是一种基于聚苯乙烯的导电热塑性化合物。导电性是通过使用特殊的导电炭黑来实现的。除了低电阻率。PRE-ELEC® PS 1326具有优良的机械性能，易于注射成型。典型应用包括静电放电敏感产品的注射成型手提箱和载带卷盘。 PRE-ELEC® PS 1326 is a conductive thermoplastic compound based on polystyrene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PS 1326 has excellent mechanical properties and is easy to injection mould. Typical applications include injection moulded tote bins and carrier tape reels for ESD sensitive products.

产品描述
厂家：	芬兰普宓斯 Premix Oy	芬兰普宓斯 Premix Oy
类别：	PS PS	PS PS
填料：
用途：	容器,装货箱	装货箱,容器
性能特点：	易加工,导电 Excellent Processability,Conductive	易加工,导电 Excellent Processability,Conductive
加工条件：	挤出 Extrusion	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL PRE-ELEC® PS 1328 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

熔体质量流动速率(200℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，21.6kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL PRE-ELEC® PS 1328 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

弯曲模量(4 mm)
Bending modulus MPa ASTM D790

弯曲模量(4 mm)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ASTM D638

拉伸强度
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

邵氏硬度(邵氏 A)
Shore hardness ISO 868

邵氏硬度(邵氏 D)
Shore hardness ISO 868

冲击性能
IMPACT PRE-ELEC® PS 1328 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-20℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(-20℃，4 mm)
Notched impact strength of cantilever beam kJ/m² ASTM D256

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180

悬臂梁无缺口冲击强度(23℃，4 mm)
Notched impact strength of cantilever beam kJ/m² ASTM D256

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-20℃，4.00 mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃，4.00 mm)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(Area)
Impact strength of cantilever beam notch ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ASTM D256

简支梁无缺口冲击强度(-20℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ASTM D256

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(-20℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ASTM D256

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL PRE-ELEC® PS 1328 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-B

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648-A

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

电气性能
ELECTRICAL PRE-ELEC® PS 1328 PRE-ELEC® PS 1326 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

表面电阻率
Surface resistivity ohms IEC 61340-2-3

加工方式

注射 PRE-ELEC® PS 1328 PRE-ELEC® PS 1326 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 速率 A (50°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 4 mm thickness

3 速率 A (50°C/h), 载荷2 (50N)