PPSU，Paryls® PPSU K1565对比PPSU，Paryls® PPSU K1550物性表,价格行情_搜料

牌号信息	Paryls® PPSU K1565 物性表 PPSU & 江门优巨指导价格：暂无塑料库存：缺货	Paryls® PPSU K1550 物性表 PPSU & 江门优巨指导价格：暂无塑料库存：缺货
牌号简介	Paryls PPSU K1565颗粒以内衬铝箔袋的纸箱提供，如果包装未受损，可以无限期储存。Paryls PPSU K1565颗粒吸收水分非常快。因此，球团在加工前需要在真空或干燥空气干燥器中在180℃下干燥至少6小时。 PARYLS® PPSU K1565 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® PPSU K1565 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 180 °C in a vacuum or dry air drier prior to processing.	PARYLS PPSU K1550颗粒在纸箱内衬铝箔袋中提供，如果包装完好，铝箔袋可以无限期地储存。PARYLS PPSU K1550颗粒吸收水分非常快。因此，球团在加工前需要在真空或干燥空气干燥器中在180℃下干燥至少6小时。 PARYLS® PPSU K1550 pellets are supplied in cartons lining aluminum foil bag, which can be stored indefinitely, provided the packaging remains undamaged. PARYLS® PPSU K1550 pellets absorb moisture very rapidly. Therefore, the pellets need to be dried at least 6h at 180 °C in a vacuum or dry air drier prior to processing.

产品描述
厂家：	江门优巨 Youju	江门优巨 Youju
类别：	PPSU PPSU	PPSU PPSU
填料：
用途：
性能特点：	防火阻燃等级V-0 V-0	防火阻燃等级V-0 V-0
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Paryls® PPSU K1565 Paryls® PPSU K1550 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4，ISO 2577

收缩率(TD)
Shrinkage rate % ISO 294-4，ISO 2577

熔体质量流动速率(365℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Paryls® PPSU K1565 Paryls® PPSU K1550 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT Paryls® PPSU K1565 Paryls® PPSU K1550 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180/A

热性能
THERMAL Paryls® PPSU K1565 Paryls® PPSU K1550 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

玻璃化转变温度
Glass transition temperature ℃ ISO 11357-2 , DSC

线性热膨胀系数(MD：23℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Paryls® PPSU K1565 Paryls® PPSU K1550 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant IEC 60250

介电常数(100 Hz)
Dielectric constant IEC 60250

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Paryls® PPSU K1565 Paryls® PPSU K1550 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 Paryls® PPSU K1565 Paryls® PPSU K1550 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

挤出 Paryls® PPSU K1565 Paryls® PPSU K1550 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

熔体温度 °C

备注

3 10°C/min

4 100V

5 K20/K20, (60*60*1 mm³)

3 10°C/min

4 100V

5 K20/K20, (60*60*1 mm³)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
挤出
备注
返回顶部

PPSU，Paryls® PPSU K1565对比PPSU，Paryls® PPSU K1550对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别