ABS，Starex LX-0951对比ABS，MAGNUM™ 8391 MED物性表,价格行情_搜料

牌号信息	Starex LX-0951 物性表 ABS & 韩国乐天尖端指导价格：暂无塑料库存：缺货	MAGNUM™ 8391 MED 物性表 ABS & 美国盛禧奥指导价格：47250.0元/吨塑料库存： 25kg
牌号简介	Starex LX-0951是一种丙烯腈丁二烯苯乙烯(ABS)产品,。它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 Starex LX-0951 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Appliances.	MAGNUM™ 8391 MED ABS具有出色的光泽外观和高流量和中等冲击性能。质量（连续加工）的ABS技术确保了一个ABS树脂，结合了良好的加工性能和稳定的光基色，是理想的自我着色。MAGNUM™ 8391 MED天然树脂已根据ISO 10993（医疗器械生物学评估）进行生物相容性测试，适用于批准的医疗应用。应用：医疗应用 MAGNUM™ 8391 MED ABS combines an excellent glossy appearance with high flow and medium impact performance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base color that is ideal for self-coloring. MAGNUM 8391 MED natural resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Applications: Medical Applications

产品描述
厂家：	韩国乐天尖端 SAMSUNG	美国盛禧奥 Trinseo
类别：	ABS ABS	ABS ABS
填料：
用途：		医疗/护理用品
性能特点：		易加工,表面光泽度好,流动性高,生物兼容性,防火阻燃等级HB Excellent Processability,Good surface appearance,High liquidity,Biocompatible,HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Starex LX-0951 MAGNUM™ 8391 MED 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183-3

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183/B

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

熔体体积流动速率(220℃，10 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(230℃，3.80kg)
Melt Flow Rate g/10min ASTM D1238

表观密度
Apparent density g/cm³ ISO 60

热性能
THERMAL Starex LX-0951 MAGNUM™ 8391 MED 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa)
Hot deformation temperature ℃ ISO 75-2 3

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/Af

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306 3

电气性能
ELECTRICAL Starex LX-0951 MAGNUM™ 8391 MED 单位
UNIT 测试方法
TEST METHOD

体积电阻
Volumetric resistance Ω.cm IEC 60093

绝缘强度()
Insulation strength KV/mm IEC 60243-1

阻燃性能
FLAMMABILITY Starex LX-0951 MAGNUM™ 8391 MED 单位
UNIT 测试方法
TEST METHOD

燃烧速率(2.0 mm)
Burning rate mm/min ISO 3795

阻燃等级(1.50 mm)
Flame retardant level UL 94

阻燃等级(1.50mm)
Flame retardant level UL-94

阻燃等级(1.60 mm)
Flame retardant level ISO 1210 3

阻燃等级(3.00 mm)
Flame retardant level UL 94

阻燃等级(3.00mm)
Flame retardant level UL-94

冲击性能
IMPACT Starex LX-0951 MAGNUM™ 8391 MED 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

简支梁冲击强度(-30℃)
Charpy impact strength ISO 179/1eU 3

简支梁冲击强度(23℃)
Charpy impact strength ISO 179/1eU 3

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 3

简支梁缺口冲击强度(-30℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA 3

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

机械性能
MECHANICAL Starex LX-0951 MAGNUM™ 8391 MED 单位
UNIT 测试方法
TEST METHOD

Nominal strain at break
Nominal strain at break % ISO 527-2 3

弯曲强度
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(3.20 mm，注塑成型)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

弯曲模量(3.20 mm，注塑成型)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服，3.20 mm，注塑成型)
Tensile strain % ISO 527-2/100

拉伸应变(屈服，3.20 mm，注塑成型)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(23℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2 3

拉伸强度(屈服，3.20 mm，注塑成型)
tensile strength MPa ISO 527-2/100

拉伸强度(屈服，3.20 mm，注塑成型)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

拉伸模量(3.20 mm，注塑成型)
Tensile modulus MPa ISO 527-2

洛氏硬度
Rockwell hardness R 级 ISO 2039-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

注射 Starex LX-0951 MAGNUM™ 8391 MED 单位测试方法

干燥时间 Hr

干燥温度 °C

水份含量 %

注塑温度模具温度 °C

注塑温度模头温度 °C

注塑温度螺筒中部温度 °C

注塑温度螺筒前部温度 °C

注塑温度螺筒后部温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.11 in/min

4 0.079 in/min

5 Thickness: 4mm

1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test.

2 一般属性：这些不能被视为规格。

3 ??????,?? ISO 10350 ??? 23°C/50%r.h. ???

4 2,0 in/min

5 0,051 in/min

6 0,079 in/min

7 3 点

8 标准 B (120°C/h), 压力1 (10N)

9 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。