XLPE，AEI SX-0670:CM424对比XLPE，GETILAN GPE/410 AF物性表,价格行情_搜料

牌号信息	AEI SX-0670:CM424 物性表 XLPE & 英国AEI Compounds 指导价格：暂无塑料库存：缺货	GETILAN GPE/410 AF 物性表 XLPE & 意大利Crosspolimeri 指导价格：暂无塑料库存：缺货
牌号简介	高柔韧性、硅烷交联、低烟、低毒、无卤的绝缘和护套用化合物，是一种非常柔韧的硅烷交联阻燃低烟无卤化合物，已开发出来，以满足有限的有毒和腐蚀性烟气排放的要求。这种化合物既可作为绝缘材料，又可作为电器软线的护套。也可用作一般电力电缆的护套材料，这里要求具有高的柔韧性和良好的热变形特性。CM424催化剂母粒通常添加在SX-0670接枝物的5%到95%之间。 Highly flexible, silane crosslinkable, low-smoke, low-toxicity, halogen-free compound for insulation and sheathing A very flexible silane cross-linkable flame-retardant low-smoke halogen-free compound, which has been developed to meet the requirements of limited toxic and corrosive fume emission. This compound is designed for use as both and insulation and sheathing in flexible cords used for appliances. It can also be used as a sheathing material for general power cable use here a combination of high flexibility and good hot deformation characteristics is required. CM424 catalyst masterbatch is normally added at 5% to 95% of SX-0670 graft.	Getilan是我们交联聚乙烯的商标。GETILAN GPE/410 AF是一种化学交联低烟低毒无卤阻燃化合物，用于绝缘和护套。它是一种易于接枝的聚乙烯，能够在水分和催化剂的存在下反应。我们通常建议我们的催化剂类型MAC/100 psf。当需要抗老化和抗铜功能时，我们建议使用MAC/202或MAC/308 PSL（反应较少）。嫁接和催化剂之间的反应这两种化合物分开储存，在开始挤压之前必须按比例混合：嫁接/催化剂97/3 GETILAN is the trade-mark of our crosslinkable polythene. GETILAN GPE/410 AF is a chemically crosslinkable low smoke and low toxicity halogen free flame retardant compound for insulation and sheathing. It is a conveniently grafted polythene able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 PSF. Where and when anti-ageing and anti-copper functions are required, we suggest our type MAC/202 or MAC/308 PSL (less in reaction). REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 97 / 3

产品描述
厂家：	英国AEI Compounds	意大利Crosspolimeri
类别：	XLPE XLPE	XLPE XLPE
填料：
用途：	阻燃绝缘,电缆护套,电器导线护套材料,电线电缆应用,阻燃护套	电缆护套
性能特点：	韧性好,低烟,可交联,无卤,阻燃 Good flexibility,Low smoke,Crosslinked,Halogen free,Flame Characteristics	可交联,自熄 Crosslinked,Self-extinguishing
加工条件：	挤出 Extrusion

技术参数

物理性能
PHYSICAL AEI SX-0670:CM424 GETILAN GPE/410 AF 单位
UNIT 测试方法
TEST METHOD

吸水率(100℃，24hr )
Water absorption rate g/m² IEC 60811

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ BS 2782 620A

熔体质量流动速率(150℃，21.6kg)
Melt Flow Rate g/10min 内部方法

熔体质量流动速率(190℃，21.6kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL AEI SX-0670:CM424 GETILAN GPE/410 AF 单位
UNIT 测试方法
TEST METHOD

拉伸应变(断裂)
Tensile strain % IEC 60811

拉伸应变(断裂)
Tensile strain % IEC 60811-1-1

拉伸强度
tensile strength MPa IEC 60811-1-1

拉伸强度(屈服)
tensile strength MPa IEC 60811

老化性能
AGING AEI SX-0670:CM424 GETILAN GPE/410 AF 单位
UNIT 测试方法
TEST METHOD

在空气中断裂时拉伸应力变化(155℃，168 hr)
Changes in tensile stress during fracture in air % IEC 60811

拉伸强度的变化率(100℃，168 hr)
The rate of change in tensile strength % IEC 60811-1-2

拉伸强度的变化率(70℃，168 hr，在水中)
The rate of change in tensile strength % IEC 60811-1-2

断裂时拉伸应力变化(100℃，168 hr)
Changes in tensile stress during fracture % IEC 60811-1-2

断裂时拉伸应力变化(70℃，168 hr，在水中)
Changes in tensile stress during fracture % IEC 60811-1-2

空气中拉伸强度的变化率(155℃，168 hr)
The rate of change in tensile strength in air % IEC 60811

热性能
THERMAL AEI SX-0670:CM424 GETILAN GPE/410 AF 单位
UNIT 测试方法
TEST METHOD

变形(80℃)
deformation IEC 60811-3-1

温度指数
Temperature index ℃ ISO 4589-3

热固性(200℃)
thermosetting % IEC 60811

热固性(Residual：200℃)
thermosetting % IEC 60811

热固性(冷却后最大永久伸长率)
thermosetting % IEC 60811-2-1

热固性(负荷下伸长率：20 N/cm²，200℃)
thermosetting % IEC 60811-2-1

阻燃性能
FLAMMABILITY AEI SX-0670:CM424 GETILAN GPE/410 AF 单位
UNIT 测试方法
TEST METHOD

Halogen Content
Halogen Content % IEC 60754-1

极限氧指数
Extreme oxygen index % ASTM D2863

极限氧指数
Extreme oxygen index % ISO 4589-2

烟气中的腐蚀性气体(pH)
Corrosive gases in flue gas IEC 60754-2

电气性能
ELECTRICAL AEI SX-0670:CM424 GETILAN GPE/410 AF 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm BS 6622

加工方式

挤出 AEI SX-0670:CM424 GETILAN GPE/410 AF 单位测试方法

口模温度 °C

头部温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

料筒5区温度 °C

备注

1 一般属性：这些不能被视为规格。

2 Cure assessment by hot set test (forced cured at 80°C in water)

1 一般属性：这些不能被视为规格。

2 20 N/cm²


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
老化性能
热性能
阻燃性能
电气性能
加工方式
挤出
备注