PBT，VALOX™ K3501 resin对比PBT，POCAN® S 1517 000000物性表,价格行情_搜料

牌号信息	VALOX™ K3501 resin 物性表 PBT & 沙特沙伯基础指导价格：66505.555元/吨塑料库存： 1000kg	POCAN® S 1517 000000 物性表 PBT & 德国恩骅力指导价格：暂无塑料库存：缺货
牌号简介	Valox K3501树脂未填充PBT，水溶性稳定，热稳定，冲击改性。一种水溶性稳定等级，设计用于改善热/湿度环境下的性能。针对需要UScar-2三级湿热性能的汽车发动机罩下应用。 Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive underhood applications requiring USCAR-2 Class III humidity/heat performance.	Pocan S 15170 000000 PBT，非增强，注塑，挤出，提高冲击强度，Pocan S 1517 000000 PBT，非增强，注塑，挤出，提高冲击强度 POCAN® S1517 000000 PBT, non-reinforced, injection molding, extrusion, improved impact strength POCAN® S1517 000000 PBT, non-reinforced, injection molding, extrusion, improved impact strength POCAN® S1517 000000 PBT, non-reinforced, injection molding, extrusion, improved impact strength

产品描述
厂家：	沙特沙伯基础 SABIC	德国恩骅力 Envalior
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：
用途：	汽车的发动机罩下的零件
性能特点：	冲击性能好,耐水解,耐高温,防潮,热稳定性好 High impact resistance,Hydrolysis stability,High Heat Resistance,Moisture resistance,Heat Stabilized	防火阻燃等级HB,冲击性能好 HB,High impact resistance
加工条件：	注射成型 Injection Molding	注射成型,挤出 Injection Molding,Extrusion

技术参数

物理性能
PHYSICAL VALOX™ K3501 resin POCAN® S 1517 000000 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD：120℃，2.0 mm，2 hrs)
Shrinkage rate % ISO 294-4

收缩率(MD：260℃，2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：110℃，2.0 mm，2 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：260℃，2.0 mm)
Shrinkage rate % ISO 294-4

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(260℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 60

机械性能
MECHANICAL VALOX™ K3501 resin POCAN® S 1517 000000 单位
UNIT 测试方法
TEST METHOD

Tensile Creep Modulus(1 hr)
Tensile Creep Modulus（1 hr） MPa ISO 899-1

弯曲应变
Bending strain %

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲强度(3.50% 应变)
bending strength MPa ISO 178-A

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178-A

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-1-2

拉伸蠕变模量(1000 hr)
Tensile creep modulus MPa ISO 899-1

标称拉伸断裂应变(23℃)
Nominal tensile fracture strain % ISO 527-2/50

球压硬度
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT VALOX™ K3501 resin POCAN® S 1517 000000 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击力峰值(-30℃)
Multi axial instrumented peak impact force N ISO 6603-2

多轴向仪器化冲击力峰值(23℃)
Multi axial instrumented peak impact force N ISO 6603-2

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ASTM D4812

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(0℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(-40℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL VALOX™ K3501 resin POCAN® S 1517 000000 单位
UNIT 测试方法
TEST METHOD

导热系数(23℃)
Thermal conductivity coefficient W/m/K ISO 8302

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ ISO 11357-3

球压测试(185℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL VALOX™ K3501 resin POCAN® S 1517 000000 单位
UNIT 测试方法
TEST METHOD

介电强度(23 ℃，1 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻率(23℃)
Volume resistivity ohms·cm IEC 60093

相对电容率(23℃，1 MHz)
Relative permittivity IEC 60250

相对电容率(23℃，100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

耗散因数(23℃，1 MHz)
Dissipation factor IEC 60250

耗散因数(23℃，100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY VALOX™ K3501 resin POCAN® S 1517 000000 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(2.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.60 mm)
Flame retardant level UL 94

补充信息
VALOX™ K3501 resin POCAN® S 1517 000000 单位
UNIT 测试方法
TEST METHOD

ISO Shortname
ISO Shortname ISO 7792

电解腐蚀
Electrolytic corrosion IEC 60426

加工方式

注射 VALOX™ K3501 resin POCAN® S 1517 000000 单位测试方法

Residual Moisture Content %

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间 - 除湿干燥剂 hr

干燥时间，最大 hr

干燥温度 °C

干燥温度 - 除湿干燥剂 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

1 一般属性：这些不能被视为规格。

2 60x60x2mm, 80°C MT, 600 bar

3 60x60x2; MT 80°C; 600 Bar

4 60x60x2

5 60x60x2mm

6 0.079 in/min

7 2 mm/min

8 Pull Rate: 2 mm/min; 50% RH

9 10°C/min

10 程序 A


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部

PBT，VALOX™ K3501 resin对比PBT，POCAN® S 1517 000000对比物性表,价格行情_搜料_soliao