牌号信息	Tritan™ MP150 物性表 PCTG & 美国伊士曼指导价格：暂无塑料库存：缺货	Tritan™ LX150HF 物性表 PCTG & 美国伊士曼指导价格：暂无塑料库存：缺货
牌号简介	伊士曼TrTi共聚酯MP150是一种高流动性的伊士曼TrTIAN。伊士曼TrTi共聚酯MP150相对于伊士曼TrTi共聚酯MP100的粘度降低40%-50%。它用于挤压涂层工艺或需要高熔体流动速率的地方。其他突出的特点包括良好的韧性，水解稳定性，耐热性和耐化学性。伊士曼TrTITE共聚酯MP150可用于食品接触应用中的限制，符合USP 35＜661＞ISO1093和ISO11607的适用和选择部分。 Eastman Tritan copolyester MP150 is a high flow grade of Eastman Tritan. Eastman Tritan copolyester MP150 has viscosity reductions of 40-50% relative to Eastman Tritan copolyester MP100. It is intended for use in extrusion coating processes or where high melt flow rate is desirable. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan copolyester MP150 may be used in food contact applications with restrictions and is compliant with applicable and select sections of USP 35 <661>, ISO10993, and ISO11607.	Eastman Tritan™ LX150HF是一种高流动性的无定形共聚酯，具有优异的外观和清晰度。伊士曼Tritan™ LX150HF相对于标准级伊士曼TrTi的粘度降低40-50%。其最突出的特点是优良的韧性、水解稳定性、耐热性和耐化学性。Tritan™ LX150HF是为化妆品、香水和个人护理市场开发的。Tritan™ LX150HF可以通过注射成型、挤出吹塑成型和注射吹塑很容易地转换成产品，用于消费者和个人护理市场。 Eastman Tritan™ LX150HF is a high flow grade of an amorphous copolyester with excellent appearance and clarity. Eastman Tritan™ LX150HF has viscosity reductions of 40-50% relative to standard grades of Eastman Tritan™. Its most outstanding features are excellent toughness, hydrolytic stability, and heat and chemical resistance. Tritan™ LX150HF was developed for the cosmetic, fragrance, and personal care markets. Tritan™ LX150HF can easily be converted into articles for application in consumer and personal care markets by injection molding, extrusion blow molding, and injection blow molding.

产品描述
厂家：	美国伊士曼 Eastman	美国伊士曼 Eastman
类别：	PCTG PCTG	PCTG PCTG
填料：
用途：	医用包装,涂层应用,药品包装	化妆品包装
性能特点：	透光性好,韧性好,流动性高,耐水解,食品接触,耐高温,耐化学性 Good Clarity,Good flexibility,High liquidity,Hydrolysis stability,Food contact compliance,High Heat Resistance,Solvent resistance	易加工,透光性好,韧性好,冲击性能好,流动性高,耐水解,成型周期快,耐高温,耐化学性,无定形的 Excellent Processability,Good Clarity,Good flexibility,High impact resistance,High liquidity,Hydrolysis stability,Quick molding cycle,High Heat Resistance,Solvent resistance,Amorphous
加工条件：	挤出涂层	挤出吹塑成型

技术参数

物理性能
PHYSICAL Tritan™ MP150 Tritan™ LX150HF 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

薄膜
Tritan™ MP150 Tritan™ LX150HF 单位
UNIT 测试方法
TEST METHOD

弹性模量(MD，铸造薄膜)
Elastic modulus MPa ASTM D882

拉伸应变(MD，断裂，挤塑薄膜)
Tensile strain % ASTM D882

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(MD，断裂，吹塑薄膜)
tensile strength MPa ASTM D882

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

薄膜厚度(测试)
film thickness µm

冲击性能
IMPACT Tritan™ MP150 Tritan™ LX150HF 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch ASTM D4812

落锤冲击(0.127 mm，铸造薄膜)
Drop hammer impact J ASTM D5420

装有测量仪表的落镖冲击(-40℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL Tritan™ MP150 Tritan™ LX150HF 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

玻璃化转变温度
Glass transition temperature ℃ DSC

光学性能
OPTICAL Tritan™ MP150 Tritan™ LX150HF 单位
UNIT 测试方法
TEST METHOD

透光率(总计)
Transmittance % ASTM D1003

雾度
Haze % ASTM D1003

机械性能
MECHANICAL Tritan™ MP150 Tritan™ LX150HF 单位
UNIT 测试方法
TEST METHOD

弯曲强度(屈服)
bending strength MPa ASTM D790

弯曲强度(屈服，23℃)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(屈服，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

特殊值
SPECIAL Tritan™ MP150 Tritan™ LX150HF 单位
UNIT 测试方法
TEST METHOD

-40℃
-40℃ J/m ASTM D256

23℃
23℃ J/m ASTM D256

加工方式

注射 Tritan™ MP150 Tritan™ LX150HF 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
薄膜
冲击性能
热性能
光学性能
机械性能
特殊值
加工方式
注射
备注
返回顶部

PCTG，Tritan™ MP150对比 PCTG，Tritan™ LX150HF对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别