PP共聚，PROTEQ™ C24UST4对比PP共聚，PROTEQ™ C24UT4物性表,价格行情_搜料

牌号信息	PROTEQ™ C24UST4 物性表 PP共聚 & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货	PROTEQ™ C24UT4 物性表 PP共聚 & 澳大利亚凯诺斯指导价格：暂无塑料库存：缺货
牌号简介	PROTEQ™ C24UST4是一种含有20%滑石填料的高熔融流动汽车聚丙烯共聚物，具有改善的热老化和紫外线性能。PROTEQ™ C24UST4的设计符合汽车内饰耐久性规范的严格要求，结合了易加工、低光泽和提高抗磨损性。典型的汽车内饰应用包括控制台、座椅垫、转向罩、车门内衬和杂物箱盖。 PROTEQ™ C24UST4 is a high melt flow automotive polypropylene copolymer containing 20% talc filler which features improved heat ageing and UV performance. PROTEQ™ C24UST4 has been designed to meet the stringent requirements of automotive interior trim durability specifications, combining easy processing with reduced gloss and improved marr resistance. Typical automotive interior applications are consoles, seat bolsters, steering shrouds, door liners and glovebox lids.	PROTEQ™ C24UT4是一种高流量20%滑石填充的紫外光稳定级聚丙烯共聚物。用于室外使用。 PROTEQ™ C24UT4 is a high flow 20% Talc filled UV stabilised grade of polypropylene copolymer. It is intended for outdoor use.

产品描述
厂家：	澳大利亚凯诺斯 Qenos	澳大利亚凯诺斯 Qenos
类别：	PP共聚 PP copolymer	PP共聚 PP copolymer
填料：	滑石粉 20	滑石粉 20
用途：	汽车内部装备,汽车领域的应用	室外应用
性能特点：	耐候抗UV,易加工,耐老化,流动性高,共聚物,热稳定性好,低光泽,防火阻燃等级HB Weather resistance is good,Excellent Processability,Good heat aging resistance,High liquidity,Copolymer,Heat Stabilized,Low Gloss,HB	耐候抗UV,流动性高,共聚物,防火阻燃等级HB Weather resistance is good,High liquidity,Copolymer,HB
加工条件：

技术参数

物理性能
PHYSICAL PROTEQ™ C24UST4 PROTEQ™ C24UT4 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD：3.0 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT PROTEQ™ C24UST4 PROTEQ™ C24UT4 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL PROTEQ™ C24UST4 PROTEQ™ C24UT4 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

阻燃性能
FLAMMABILITY PROTEQ™ C24UST4 PROTEQ™ C24UT4 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ AS/NZS 60695.2.12

灼热丝起燃温度(1.6 mm)
Igniting temperature of the hot wire ℃ AS/NZS 60695

机械性能
MECHANICAL PROTEQ™ C24UST4 PROTEQ™ C24UT4 单位
UNIT 测试方法
TEST METHOD

弯曲强度(3.20 mm)
bending strength MPa ASTM D790

弯曲模量(3.20 mm)
Bending modulus MPa ASTM D790

拉伸应变(断裂，3.20 mm)
Tensile strain % ASTM D638

拉伸强度(3.20 mm)
tensile strength MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，15 秒)
Shore hardness ISO 868

加工方式

注射 PROTEQ™ C24UST4 PROTEQ™ C24UT4 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度 PROTEQ™ C24UST4 PROTEQ™ C24UT4 单位测试方法

背压 MPa

螺杆转速 rpm

锁模力 kN/cm²

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.39 in/min

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 0.051 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
机械性能
加工方式
注射
注射速度
备注
返回顶部