技术参数
物理性能 PHYSICAL
Halar® 500LC
Halar® 5001C
单位 UNIT
测试方法 TEST METHOD
吸水率(平衡)
Water absorption rate
%
ASTM D570
密度
Density
g/cm³
ASTM D792
收缩率(MD)
Shrinkage rate
%
ASTM D955
收缩率(MD)
Shrinkage rate
%
ASTM D995
熔体质量流动速率(275℃,2.16kg)
Melt Flow Rate
g/10min
ASTM D1238
熔体质量流动速率(饱和吸水量)
Melt Flow Rate
%
ASTM D570
热性能 THERMAL
Halar® 500LC
Halar® 5001C
单位 UNIT
测试方法 TEST METHOD
导热系数
Thermal conductivity coefficient
W/m/K
JIS R2618
导热系数(40℃)
Thermal conductivity coefficient
W/m/K
ASTM C177
比热容
Specific heat capacity
J/Kg/℃
ASTM C351
比热(23℃)
specific heat
J/kg/℃
ASTM D3418
热变形温度(0.45 MPa,未退火)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃
ASTM D648
热稳定性(1%质量损失,N2)
thermal stability
℃
TGA
熔融温度
Melting temperature
℃
熔融温度
Melting temperature
℃
ASTM D3418
玻璃化转变温度
Glass transition temperature
℃
ASTM D648
玻璃化转变温度
Glass transition temperature
℃
DMA
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
1/℃
ASTM D696
结晶峰温度(DSC)
Crystallization peak temperature
℃
ASTM D3418
结晶温度
Crystallization temperature
℃
ASTM D3418
结晶热
Crystallization heat
J/g
ASTM D3418
维卡软化温度
Vicat Softening Temp
脆化温度
Embrittlement temperature
℃
ASTM D746
脆化温度
Embrittlement temperature
℃
ASTM D746A
融合热
Fusion heat
J/g
ASTM D3418
融合热量
Fusion heat
J/g
ASTM D3418
电气性能 ELECTRICAL
Halar® 500LC
Halar® 5001C
单位 UNIT
测试方法 TEST METHOD
介电常数(23 ℃,1 MHz)
Dielectric constant
ASTM D150
介电常数()
Dielectric constant
1 MHz
ASTM D150
介电强度(23 ℃,3.2 mm)
Dielectric strength
kV/mm
ASTM D149
体积电阻
Volumetric resistance
Ω.cm
ASTM D257
体积电阻率(23℃)
Volume resistivity
ohms·cm
ASTM D257
绝缘强度(3.18 mm)
Insulation strength
KV/mm
ASTM D149
阻燃性能 FLAMMABILITY
Halar® 500LC
Halar® 5001C
单位 UNIT
测试方法 TEST METHOD
极限氧指数
Extreme oxygen index
%
ASTM D2863
阻燃等级
Flame retardant level
UL 94
阻燃等级()
Flame retardant level
V-0
UL 94
冲击性能 IMPACT
Halar® 500LC
Halar® 5001C
单位 UNIT
测试方法 TEST METHOD
悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(-40℃,3.2mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
J/m
ASTM D256
悬臂梁缺口冲击强度(23℃,3.2mm)
Impact strength of cantilever beam notch
ASTM D256
机械性能 MECHANICAL
Halar® 500LC
Halar® 5001C
单位 UNIT
测试方法 TEST METHOD
弯曲强度(2.50 mm/min,23℃)
bending strength
MPa
ASTM D790
弯曲强度(23℃)
bending strength
MPa
ASTM D790
弯曲模量(2.50 mm/min,23℃)
Bending modulus
MPa
ASTM D790
弯曲模量(23℃)
Bending modulus
MPa
ASTM D790
拉伸应变(屈服,23℃)
Tensile strain
%
ASTM D638
拉伸应变(断裂,23℃)
Tensile strain
%
ASTM D638
拉伸强度(屈服,23℃)
tensile strength
MPa
ASTM D638
拉伸强度(屈服,23℃,50 mm/min )
tensile strength
MPa
ASTM D638
拉伸强度(断裂,23℃)
tensile strength
MPa
ASTM D638
拉伸强度(断裂,23℃,50 mm/min )
tensile strength
MPa
ASTM D638
拉伸模量(23℃)
Tensile modulus
MPa
ASTM D638
拉伸模量(23℃,50 mm/min )
Tensile modulus
MPa
ASTM D638
摩擦系数(与自身 - 动态)
friction coefficient
ASTM D1894
摩擦系数(与自身 - 静态)
friction coefficient
ASTM D1894
泰伯耐磨性(1000 周期,500 g,CS-17 转轮)
Taber abraser
mg
洛氏硬度
Rockwell hardness
R 级
ASTM D785
洛氏硬度(R 级)
Rockwell hardness
ASTM D785
磨擦系数(动态)
Friction coefficient
ASTM D3702
磨擦系数(屈服)
Friction coefficient
%
ASTM D638
磨擦系数(拉伸应变)
Friction coefficient
磨擦系数(泰伯磨损)
Friction coefficient
mg/1000cy
ASTM D1044
磨擦系数(静态)
Friction coefficient
ASTM D3702
邵氏硬度(邵氏 A)
Shore hardness
ASTM D2240
邵氏硬度(邵氏 D)
Shore hardness
ASTM D2240