PA612，RTP 203.3D对比PA612，RTP 205D HS物性表,价格行情_搜料

牌号信息	RTP 203.3D 物性表 PA612 & 美国RTP 指导价格：暂无塑料库存：缺货	RTP 205D HS 物性表 PA612 & 美国RTP 指导价格：暂无塑料库存：缺货
牌号简介	该材料的状态为“商业：限量发行”。该材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。与大多数玻璃填充尼龙相比，RTP 200D系列材料具有更好的尺寸稳定性、韧性和更低的吸水性。它们还具有良好的可塑性和流动性。-每个RTP公司的初步产品数据- Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. The RTP 200D series materials have better dimensional stability, toughness, and lower water absorption than most other glass filled nylons. They also display good moldability and ease of flow. -Preliminary Product Data per RTP Co.-	警告：此材料的状态为“商业：限量发行”。此材料的数据最近尚未验证。在指定此等级之前，请联系RTP公司以获取当前信息。 Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade.

产品描述
厂家：	美国RTP	美国RTP
类别：	PA612 PA612	PA612 PA612
填料：
用途：
性能特点：	防火阻燃等级HB HB	热稳定性好,防火阻燃等级HB Heat Stabilized,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL RTP 203.3D RTP 205D HS 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

冲击性能
IMPACT RTP 203.3D RTP 205D HS 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL RTP 203.3D RTP 205D HS 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

电气性能
ELECTRICAL RTP 203.3D RTP 205D HS 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电强度
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

耐电弧性
Arc resistance sec ASTM D495

耗散因数(1 MHz)
Dissipation factor ASTM D150

阻燃性能
FLAMMABILITY RTP 203.3D RTP 205D HS 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

机械性能
MECHANICAL RTP 203.3D RTP 205D HS 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

加工方式

注射 RTP 203.3D RTP 205D HS 单位测试方法

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

备注


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
机械性能
加工方式
注射
备注
返回顶部

PA612，RTP 203.3D对比PA612，RTP 205D HS对比物性表,价格行情_搜料_soliao