PP均聚，Retpol® 200 GF HS对比PP均聚，Extron® 200 GF HS物性表,价格行情_搜料

牌号信息	Retpol® 200 GF HS 物性表 PP均聚 & 澳大利亚PolyPacific 指导价格：暂无塑料库存：缺货	Extron® 200 GF HS 物性表 PP均聚 & 澳大利亚PolyPacific 指导价格：暂无塑料库存：缺货
牌号简介	Exron 200 GF HS是一种20%玻璃纤维增强均聚聚丙烯化合物。它是一种低流量注射成型等级为需要高热变形温度和低模具收缩刚性部件开发。在150°C条件下，它能够稳定地满足500小时的汽车热老化要求。 Extron 200 GF HS is a 20% glass fibre reinforced homopolymer polypropylene compound. It is a low flow injection moulding grade developed for rigid components requiring high heat deflection temperatures and low mould shrinkages. It is stabilized to meet automotive heat ageing requirements of 500hrs at 150°C.	Extron® 200 GF HS是一种20%玻璃纤维增强均聚聚丙烯化合物。它是一种低流量注射成型等级为需要高热变形温度和低模具收缩刚性部件开发。在150°C条件下，它能够稳定地满足500小时的汽车热老化要求。 Extron 200 GF HS is a 20% glass fibre reinforced homopolymer polypropylene compound. It is a low flow injection moulding grade developed for rigid components requiring high heat deflection temperatures and low mould shrinkages. It is stabilized to meet automotive heat ageing requirements of 500hrs at 150°C.

产品描述
厂家：	澳大利亚PolyPacific	澳大利亚PolyPacific
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	玻璃纤维 20	玻璃纤维 20
用途：	汽车领域的应用	汽车领域的应用
性能特点：	流动性低,收缩性低,热稳定性好,均聚物 Low liquidity,Low contractility,Heat Stabilized,Homopolymer	流动性低,收缩性低,热稳定性好,均聚物 Low liquidity,Low contractility,Heat Stabilized,Homopolymer
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Retpol® 200 GF HS Extron® 200 GF HS 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD：3.0 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT Retpol® 200 GF HS Extron® 200 GF HS 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(3 mm)
Notched impact strength of cantilever beam J/m ASTM D256

悬臂梁缺口冲击强度(3mm)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Retpol® 200 GF HS Extron® 200 GF HS 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.0 mm)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，3.0 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.00 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.00 mm)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：-30~30℃，3.00 mm)
Linear coefficient of thermal expansion 1/℃ ASTM D696

机械性能
MECHANICAL Retpol® 200 GF HS Extron® 200 GF HS 单位
UNIT 测试方法
TEST METHOD

弯曲模量(3 mm)
Bending modulus MPa ASTM D790

拉伸应变(断裂，3 mm)
Tensile strain % ASTM D638

拉伸强度(3 mm)
tensile strength MPa ASTM D638

洛氏硬度(R 级，3.00 mm)
Rockwell hardness ASTM D785

邵氏硬度(邵氏 D，15 秒，3.00 mm)
Shore hardness

邵氏硬度(邵氏 D，15 秒，3.00 mm)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D，3.00 mm)
Shore hardness

邵氏硬度(邵氏 D，3.00 mm)
Shore hardness ASTM D2240

加工方式

注射 Retpol® 200 GF HS Extron® 200 GF HS 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大回制料比例 %

模具温度 °C

注射速度

注射速度 Retpol® 200 GF HS Extron® 200 GF HS 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 2,0 in/min

2. 50 mm/min