PPS，LNP™ THERMOCOMP™ OF008AE compound对比PPS，Ryton® R-4-232BL物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ OF008AE compound 物性表 PPS & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Ryton® R-4-232BL 物性表 PPS & 比利时索尔维指导价格：189000.0元/吨塑料库存： 5275kg
牌号简介	LNPThermocompOF008AE是一种基于PPS-支化树脂的化合物，含有40%的玻璃纤维。这个等级的附加特征是：容易成型。也称为：lnpThermocomp化合物of-1008 em产品再订购名称：of008ae LNP* THERMOCOMP* OF008AE is a compound based on PPS - Branched resin containing 40% Glass Fiber. Added feature of this grade is: Easy Molding.	Ryton® R-4-232BL 40%玻璃纤维增强聚苯硫醚化合物符合美国食品药品监督管理局（FDA）、NSF51和欧盟（欧盟10/2011）的规定，用作与所有类型食品接触的重复使用物品的成分。它还被NSF61、KTW和ACS批准用于饮用水系统。 Ryton® R-4-232BL 40% glass fiber reinforced polyphenylene sulfide compound complies with United States Food and Drug Administration (FDA), NSF51, and European Union (EU 10/2011) regulations for use as a component of articles intended for repeat use in contact with all types of foods. It has also been approved for drinking water systems by NSF61, KTW and ACS.

产品描述
厂家：	沙特沙伯基础 SABIC	比利时索尔维 Solvay
类别：	PPS PPS	PPS PPS
填料：	玻璃纤维 40	玻璃纤维 40
用途：		家电部件
性能特点：	易加工,支化高分子结构 Excellent Processability,Branched polymer structure	食品接触,防火阻燃等级V-0,防火阻燃等级5VA Food contact compliance,V-0,5VA
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ OF008AE compound Ryton® R-4-232BL 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：3.2 mm)
Shrinkage rate %

机械性能
MECHANICAL LNP™ THERMOCOMP™ OF008AE compound Ryton® R-4-232BL 单位
UNIT 测试方法
TEST METHOD

压缩强度
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ASTM D790

弯曲强度(断裂，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2

泊松比
Poisson's ratio ISO 527

洛氏硬度(M 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT LNP™ THERMOCOMP™ OF008AE compound Ryton® R-4-232BL 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ OF008AE compound Ryton® R-4-232BL 单位
UNIT 测试方法
TEST METHOD

UL温度额定值
UL temperature rating ℃ UL 746B

导热系数
Thermal conductivity coefficient W/m/K

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(100 到 200℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(50 到 100℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(50℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(MD)
Linear coefficient of thermal expansion ASTM E831

线性热膨胀系数(MD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(TD)
Linear coefficient of thermal expansion ASTM E831

线性热膨胀系数(TD：-30~30℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ OF008AE compound Ryton® R-4-232BL 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.39 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

加工方式

注射 LNP™ THERMOCOMP™ OF008AE compound Ryton® R-4-232BL 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0,20 in/min

3 类型 1, 0,20 in/min

4 0,051 in/min

5 0,079 in/min

6 80*10*4

7 80*10*4 mm

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注
返回顶部