ABS，KumhoSunny ABS HU600-P对比ABS，Sinkral® C 442物性表,价格行情_搜料

牌号信息	KumhoSunny ABS HU600-P 物性表 ABS & 上海锦湖日丽指导价格：暂无塑料库存：缺货	Sinkral® C 442 物性表 ABS & 意大利Versalis 指导价格：暂无塑料库存：缺货
牌号简介	ABSHU600-P是一种高耐热的ABS电镀树脂，具有高刚性和高冲击性。 ABSHU600-P is a high heat resistance ABS resion for plating , offering high rigidity and high impact.	Sinkral® C 442是一种耐热注塑级产品，具有良好的流动性和抗冲击性，在加工过程中具有优异的热稳定性。名称：热塑性ISO 2580-abs 1，MGN，105-08-16-20由于黄色指数低且颜色稳定，因此适用于自着色，主要用于汽车行业的内饰（挤压型材、内饰等），以及适当的母版，用于格栅和后视镜等外部零件。等级有天然或彩色两种。 Sinkral C 442 is a heat resistant injection moulding grade offering good flow and impact resistance together with excellent thermal stability during processing. Designation: Thermoplastic ISO 2580-ABS 1,MGN,105-08-16-20 Thanks to a low Yellow Index and colour constancy, it is suitable for selfcolouring, mainly in the automotive industry for interior (extruded profiles, interior trim,..) and with proper masterbatches, for exterior parts such as grilles and rear view mirrors. Grade available either in natural or coloured versions.

产品描述
厂家：	上海锦湖日丽 KumhoSunny	意大利Versalis
类别：	ABS ABS	ABS ABS
填料：
用途：		汽车内部装备,汽车领域的应用,汽车外部零件
性能特点：	机械强度好,冲击性能好,耐高温,电镀 Good Rigidity,High impact resistance,High Heat Resistance,Electroplating	冲击性能好,易流动,颜色稳定,耐高温,热稳定性好,防火阻燃等级HB High impact resistance,Good liquidity,Good color stability,High Heat Resistance,Heat Stabilized,HB
加工条件：	注射成型 Injection Molding	型材挤出成型 Profile extrusion

技术参数

物理性能
PHYSICAL KumhoSunny ABS HU600-P Sinkral® C 442 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate % 内部方法

收缩率(23℃ )
Shrinkage rate % ISO 294-4

熔体质量流动速率(220℃，10.0kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL KumhoSunny ABS HU600-P Sinkral® C 442 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度(64 mm)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量(64 mm)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度
tensile strength MPa ASTM D638

拉伸强度
tensile strength MPa ISO 527-2/50

泊松比
Poisson's ratio ISO 527

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

冲击性能
IMPACT KumhoSunny ABS HU600-P Sinkral® C 442 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180

悬臂梁缺口冲击强度(-20℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-40℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

悬臂梁缺口冲击强度(0℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch J/m ISO 180-4A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength ISO 179

简支梁无缺口冲击强度(-40℃)
Charpy Unnotch Impact strength DIN 53453

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength DIN 53453

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² DIN 53453

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL KumhoSunny ABS HU600-P Sinkral® C 442 单位
UNIT 测试方法
TEST METHOD

导热系数
Thermal conductivity coefficient W/m/K ASTM C177

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM D696

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ISO 306/A120

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL KumhoSunny ABS HU600-P Sinkral® C 442 单位
UNIT 测试方法
TEST METHOD

介电常数(1 kHz)
Dielectric constant IEC 60250

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

耗散因数(1 kHz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY KumhoSunny ABS HU600-P Sinkral® C 442 单位
UNIT 测试方法
TEST METHOD

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

阻燃等级(1.50 mm)
Flame retardant level UL 94

补充信息
KumhoSunny ABS HU600-P Sinkral® C 442 单位
UNIT 测试方法
TEST METHOD

Designation
Designation

加工方式

注射 KumhoSunny ABS HU600-P Sinkral® C 442 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

挤出 KumhoSunny ABS HU600-P Sinkral® C 442 单位测试方法

干燥时间 hr

干燥温度 °C

熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 Condition: 4 J

4 Condition: 5.5 J

5 120°C/h

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 0.079 in/min

4 4 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
挤出
备注
返回顶部