PPO(PPE)+PO，NORYL™ WCV065 resin对比PPO(PPE)+PO，FLEX NORYL™ Resin WCD883CU物性表,价格行情_搜料

牌号信息	NORYL™ WCV065 resin 物性表 PPO(PPE)+PO & 沙特沙伯基础指导价格：暂无塑料库存：缺货	FLEX NORYL™ Resin WCD883CU 物性表 PPO(PPE)+PO & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	柔性、非卤化FR、PPE+聚烯烃树脂，设计用于汽车ISO6722 A级应用的评估。 Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications.	用于评估HD 21.14软电缆护套等应用的柔性、抗紫外线和非卤化阻燃挤出级。阻燃性能满足EN 50265-2-1要求。88肖氏硬度A。通常在标准挤压设备上进行的加工。用0.12 mm x 20股铜导线在2.0 mm导线上进行的导线试验。 Flexible, UV resistant and non-halogenated flame retardant extrusion grade intended for evaluation in applications such as jacket of HD 21.14 flexible cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. 88 Shore A hardness. Processing typically conducted on standard extrusion equipment. Wire tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PO PPO(PPE)+Polyolefin	PPO(PPE)+PO PPO(PPE)+Polyolefin
填料：
用途：	汽车领域的应用	电气/电子应用领域
性能特点：	韧性好,无卤,阻燃 Good flexibility,Halogen free,Flame Characteristics	耐候抗UV Weather resistance is good
加工条件：	挤出涂层

技术参数

物理性能
PHYSICAL NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(250℃，10.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(100 mm跨距)
Bending modulus MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % UL 1581

拉伸应变(断裂，80℃)
Tensile strain % UL 1581

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa UL 1581

拉伸强度(断裂，80℃)
tensile strength MPa UL 1581

拉伸模量
Tensile modulus MPa ISO 527-1-2

邵氏硬度(邵氏 A，30 秒)
Shore hardness ASTM D2240

邵氏硬度(邵氏 D，30 秒)
Shore hardness ASTM D2240

冲击性能
IMPACT NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(-30℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位
UNIT 测试方法
TEST METHOD

Heat Deformation(100℃)
Heat Deformation（100℃） % UL 1581

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 9

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

脆化温度
Embrittlement temperature ℃ ASTM D746

电气性能
ELECTRICAL NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位
UNIT 测试方法
TEST METHOD

介电常数(1.10 GHz)
Dielectric constant 内部方法

介电强度(2 mm，在油中)
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm ASTM D257

相对电容率(1 MHz)
Relative permittivity IEC 60250

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(1.1 GHz)
Dissipation factor 内部方法

表面电阻率
Surface resistivity ohms ASTM D257

阻燃性能
FLAMMABILITY NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位
UNIT 测试方法
TEST METHOD

Vertical Flame Test
Vertical Flame Test EN 50265-2-1

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(3.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(3 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

加工方式

挤出 NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒1区温度 °C

料筒3区温度 °C

料筒5区温度 °C

熔体温度 °C

挤压说明 NORYL™ WCV065 resin FLEX NORYL™ Resin WCD883CU 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 类型 1, 2,0 in/min

3 0,051 in/min

4 0,079 in/min

5 Yield

6 80*10*4 sp=62mm

7 80*10*4

8 80*10*4 mm

9 标准 B (120°C/h), 载荷2 (50N)

2. 2.0 mm wire with 0.12 mm x 20 stranded copper

3. 类型 1, 50 mm/min

4. After 7 days. Tested on 2.0 mm wire with 0.12 mm x 20 stranded copper

5. 6 days, 2.0 mm wire with 0.12 mm x 20 stranded copper

6. 13 mm/min

7. 250g, 2.0 mm wire with 0.12 mm x 20 stranded copper

8. UL 1581 tested on 2.0 mm wire with 0.12 mm x 20 stranded copper


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
挤出
挤压说明
备注