PP均聚，Bormed™ HD810MO对比PP均聚，TOTAL Polypropylene PPH 6088物性表,价格行情_搜料

牌号信息	Bormed™ HD810MO 物性表 PP均聚 & 奥地利北欧化工指导价格：23100.0元/吨塑料库存： 1000kg	TOTAL Polypropylene PPH 6088 物性表 PP均聚 & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	Bormed™ HD810MO是一种聚丙烯均聚物，该聚合物等级用于生产医疗和医疗相关物品。此外，它还可以用γ射线进行消毒，具有良好的耐化学性。如果储存温度低于40°C，用这种级别的材料制成的辐射剂量为25 kgy的产品的保质期为5年。 Bormed HD810MO is a resin intended for evaluation for use in Healthcare applications. Bormed HD810MO is a nucleated polypropylene homopolymer with a medium melt flow rate. Bormed HD810MO is specially formulated for production of articles which need to be sterilized with radiation (gamma and beta radiation). Tests on specimen radiated at 25 kGy have shown stability for 5 years when stored at room temperature. Material can also well be sterilised with ethylene oxide or steam. Applications Bormed HD810MO has been evaluated according to different regulations and norms. Typical applications are mentioned below for Medical devices or Pharmaceutical & Diagnostic packaging. However, Borealis should be consulted for final approval to evaluate the use of Bormed HD810MO . Disposable non pre-filled syringes Catheter Blood collection systems Laboratory disposable This grade may only be used for the applications listed in the Product Datasheet and only to the extent that the application is within the scope of the tests set out in the Statement on Compliance to Regulations on Medical Use for that grade. If an application is not listed in the Product Datasheet, the grade can be used for such application only after express written consent of the Borealis Marketing Manager, Healthcare. Borealis prohibits the use of any healthcare grade product in an implantable device that is introduced into the human body by surgical intervention and that is intended to remain in place following surgical procedure. Special features Radiation resistance High transparency	聚丙烯PPH 6088是一种均聚物，其熔体流动指数为9 g/10 min，用于薄膜的挤出成型，具有优异的光学性能和杀菌性能。聚丙烯PPH 6088采用防滑、防堵剂配制而成。建议用于食品包装、纺织品包装、花卉包装、层压膜和文具。 Polypropylene PPH 6088 is a homopolymer with a Melt Flow Index of 9 g/10 min for the cast extrusion of films with excellent optical properties and good sterilizability. Polypropylene PPH 6088 is formulated with slip and anti-block agents. It is recommended for food packaging, textile packaging, flowers packaging, lamination films and stationary supplies.

产品描述
厂家：	奥地利北欧化工 Borealis AG	法国道达尔 TOTAL
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	医疗/护理用品	包装,层压板,流延薄膜,食品包装,文具
性能特点：	易加工,透光性好,可回收,易流动,印刷性好,抗伽马射线,辐射消毒,耐化学性,均聚物 Excellent Processability,Good Clarity,Renewable resources,Good liquidity,Good Printability,Gamma radiation,Radiation disinfection,Solvent resistance,Homopolymer	高光滑性,易消毒,光学性能,抗结块性,均聚物 Smoothness,Good disinfection,Optical performance,High anti-blocking,Homopolymer
加工条件：	注射成型 Injection Molding	薄膜挤出 Film extrusion

技术参数

物理性能
PHYSICAL Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate %

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³ ISO 1183

冲击性能
IMPACT Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度(DSC)
Melting temperature ℃ ISO 3146

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

机械性能
MECHANICAL Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

薄膜
Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

埃尔曼多夫抗撕强度(MD：50 µm，铸造薄膜)
Elmandorf tear strength N ISO 6383-2

埃尔曼多夫抗撕强度(TD：50 µm，铸造薄膜)
Elmandorf tear strength N ISO 6383-2

拉伸应变(MD，断裂，50 µm，铸造薄膜)
Tensile strain % ISO 527-3

拉伸应变(TD，断裂，50 µm，铸造薄膜)
Tensile strain % ISO 527-3

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸强度(MD，屈服，50 µm，吹塑薄膜)
tensile strength MPa ISO 527-3

拉伸强度(TD，屈服，50 µm，吹塑薄膜)
tensile strength MPa ISO 527-3

拉伸强度(屈服)
tensile strength MPa ISO 527-2

落锤冲击(50 µm，铸造薄膜)
Drop hammer impact g ISO 7765-1

薄膜厚度(测试)
film thickness µm

光学性能
OPTICAL Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

光泽度(45°，50.0 µm，铸造薄膜)
gloss ASTM D2457

雾度(50 µm，铸造薄膜)
Haze % ISO 14782

特殊值
SPECIAL Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位
UNIT 测试方法
TEST METHOD

MD，断裂，50 µm，吹塑薄膜
MD, fracture, 50 µ m, blow molded film MPa ISO 527-3

TD，断裂，50 µm，吹塑薄膜
TD, fracture, 50 µ m, blow molded film MPa ISO 527-3

加工方式

注射 Bormed™ HD810MO TOTAL Polypropylene PPH 6088 单位测试方法

保压 MPa

加工熔体温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 Injection molded specimen

1 SiO2

2 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
薄膜
光学性能
特殊值
加工方式
注射
备注
返回顶部

PP均聚，Bormed™ HD810MO对比PP均聚，TOTAL Polypropylene PPH 6088对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别