PPO(PPE)+PS+PA，NORYL GTX™ NX0031 resin对比PPO(PPE)+PS+PA，NORYL GTX™ GTX673 resin物性表,价格行情_搜料

牌号信息	NORYL GTX™ NX0031 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：暂无塑料库存：缺货	NORYL GTX™ GTX673 resin 物性表 PPO(PPE)+PS+PA & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	NORYL GTX™ NX0031 resin是一种导电树脂，专门为静电喷涂和粉末涂料应用而设计。这种材料具有高冲击性、良好的流动性和导电性。该材料仅提供黑色，适用于注塑成型。 NORYL GTX NX0031 resin is a conductive resin specially designed for electrostatic painting and powder coating applications. This material combines high impact, good flow and conductivity. The material is only available in black and is suitable for injection molding.	导电noryl GTX树脂设计用于型材挤压。该等级可以是静电或粉末涂料，无需底漆。此外，它的高热性能允许它与金属在同一条线上涂漆。 Conductive NORYL GTX resin designed for profile extrusion. This grade can be electrostatic or powder coat painted without the need for a primer. In addition, its high heat capability allows it to be painted on the same line as metal.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PPO(PPE)+PS+PA PPO(PPE)+PS+PA	PPO(PPE)+PS+PA PPO(PPE)+PS+PA
填料：
用途：
性能特点：	冲击性能好,导电,易流动,可表面喷涂 High impact resistance,Conductive,Good liquidity,Sprayable	可表面喷涂,耐高温 Sprayable,High Heat Resistance
加工条件：	注射成型 Injection Molding	型材挤出成型 Profile extrusion

技术参数

物理性能
PHYSICAL NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792 , ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(280℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(300℃，5 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(280℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(300℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(125℃)
Ball pressure test IEC 60695-10-2

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~60℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525 10 , ISO 306/B50 10

电气性能
ELECTRICAL NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm 内部方法

加工方式

注射 NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位测试方法

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议的最大水分含量 %

建议注射量 NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

挤出 NORYL GTX™ NX0031 resin NORYL GTX™ GTX673 resin 单位测试方法

口模温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

接头温度 °C

料筒1区温度 °C

料筒2区温度 °C

料筒3区温度 °C

料筒4区温度 °C

校准温度，首次 °C

熔体温度 °C

备注

3 5.0 mm/min

4 类型 1, 50 mm/min

5 1.3 mm/min

6 2.0 mm/min

7 Yield

8 80*10*4 sp=62mm

9 80*10*4

10 标准 B (120°C/h), 载荷2 (50N)

2 5.0 mm/min

3 类型 1, 50 mm/min

4 1.3 mm/min

5 2.0 mm/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 80*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
建议注射量
挤出
备注
返回顶部

PPO(PPE)+PS+PA，NORYL GTX™ NX0031 resin对比PPO(PPE)+PS+PA，NORYL GTX™ GTX673 resin对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别