牌号信息	TRANSMARE® BIO M106 物性表 PLA & 荷兰Transmare 指导价格：暂无塑料库存：缺货	TRANSMARE® BIO 35MI-10-0.001 物性表 PLA & 荷兰Transmare 指导价格：暂无塑料库存：缺货
牌号简介	TRANSMARE® BIO M106是一种以改性聚乳酸为基础的不透明颗粒，在熔融物中具有良好的氧化性、颜色和分子量稳定性，可生物降解，/可堆肥：TRANSMARE® BIO M106是基于根据DIN EN 13432:2000-12和ASTM D 6400:1999认证的材料，主要基于可再生原材料TRANSMARE® BIO M106，可在定制颜色 TRANSMARE® BIO M106 is a non-transparent granulate based on modified polylactic acid Good oxidation-, colour- and molecular weight stability in the melt Biodegradable,/Compostable: TRANSMARE® BIO M106 is based on materials that are certified according to DIN EN 13432:2000-12 and ASTM D 6400:1999 Predominantly based on renewable raw materials TRANSMARE® BIO M106 can be provided in custom colours	TRANSMARE® BIO 35MI-10-0.001是一种具有良好流动性和冲击性能的基于PLA-Ingeo的冲击改性生物聚合物。 TRANSMARE® BIO 35MI-10-0.001 is a PLA INGEO™ based impact modified biopolymer with good flow and impact properties.

产品描述
厂家：	荷兰Transmare	荷兰Transmare
类别：	PLA PLA	PLA PLA
填料：
用途：
性能特点：	可回收,生物可降解,颜色稳定,可堆肥 Renewable resources,Biodegradable,Good color stability,Compostable	机械强度好,冲击性能好,可回收,易流动 Good Rigidity,High impact resistance,Renewable resources,Good liquidity
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL TRANSMARE® BIO M106 TRANSMARE® BIO 35MI-10-0.001 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ISO 1183

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL TRANSMARE® BIO M106 TRANSMARE® BIO 35MI-10-0.001 单位
UNIT 测试方法
TEST METHOD

弯曲强度(注塑成型)
bending strength MPa ISO 178

弯曲模量(注塑成型)
Bending modulus MPa ISO 178

拉伸应变(屈服，4 mm，注塑成型)
Tensile strain % ISO 527-2/50

拉伸应变(断裂，4 mm，注塑成型)
Tensile strain % ISO 527-2/50

拉伸强度(屈服，4 mm，注塑成型)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂，4 mm，注塑成型)
tensile strength MPa ISO 527-2/50

拉伸模量(4 mm，注塑成型)
Tensile modulus MPa ISO 527-1-2

拉伸模量(4 mm，注塑成型)
Tensile modulus MPa ISO 527-2/50

邵氏硬度(邵氏 D)
Shore hardness ISO 868

邵氏硬度(邵氏 D，注塑成型)
Shore hardness ISO 868

冲击性能
IMPACT TRANSMARE® BIO M106 TRANSMARE® BIO 35MI-10-0.001 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃，注塑成型)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-20℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(-40℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(0℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃，注塑成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-40℃，注塑成型)
Charpy Unnotch Impact strength kJ/m² ISO 179/1U

简支梁无缺口冲击强度(23℃，注塑成型)
Charpy Unnotch Impact strength ISO 179/1U

简支梁缺口冲击强度(-20℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(-40℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(0℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

简支梁缺口冲击强度(23℃，注塑成型)
Charpy Notched Impact Strength kJ/m² ISO 179/1A

热性能
THERMAL TRANSMARE® BIO M106 TRANSMARE® BIO 35MI-10-0.001 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

加工方式

注射 TRANSMARE® BIO M106 TRANSMARE® BIO 35MI-10-0.001 单位测试方法

Dew Point - 热风干燥机 °C

加工熔体温度 °C

射嘴温度 °C

干燥时间 - 热风干燥机 hr

干燥温度 - 热风干燥机 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注射速度

备注

1 一般属性：这些不能被视为规格。

2 0.079 in/min

1 一般属性：这些不能被视为规格。

2 0.079 in/min

3 3-point bending


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部