PA6，Ultramid® B3WG10 BK00564对比PA6，AKROMID® B3 GF 50 1 natural (2531)物性表,价格行情_搜料

牌号信息	Ultramid® B3WG10 BK00564 物性表 PA6 & 德国巴斯夫指导价格：暂无塑料库存：缺货	AKROMID® B3 GF 50 1 natural (2531) 物性表 PA6 & 德国AKRO-PLASTIC 指导价格：暂无塑料库存：缺货
牌号简介	该树脂是一种热稳定的50%玻璃纤维增强PA6注射成型化合物，具有优异的强度、刚度、高温性能和尺寸稳定性。它可以在自然，黑色耐候和色素版本。应用Ultramid® B3WG10 BK00564通常推荐用于电动工具外壳、牛耳标记器、行李架、风扇和压力调节器外壳等应用。 This resin is a heat stabilized, 50% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is available in natural, black weather resistant and pigmented versions. Applications Ultramid B3WG10 BK00564 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.	AKROMID® B3 GF 50 1 natural (2531)是一种50%玻璃纤维增强、热稳定的聚酰胺6，具有很高的刚度和强度，其固有颜色轻，主要应用于机械工程和汽车工业。 AKROMID® B3 GF 50 1 natural (2531) is a 50% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength and light inherent color Components in mechanical engineering and in the automotive industry

产品描述
厂家：	德国巴斯夫 BASF	德国AKRO-PLASTIC
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 50	玻璃纤维 50
用途：	皮箱,外壳,动力/其它工具	工程应用
性能特点：	机械强度好,尺寸稳定性好,耐油,热稳定性好 Good Rigidity,Good Dimensional Stability,Grease resistance,Heat Stabilized	机械强度好,热稳定性好,防火阻燃等级HB Good Rigidity,Heat Stabilized,HB
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位
UNIT 测试方法
TEST METHOD

吸水率(70℃，62% RH )
Water absorption rate % ISO 1110

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 294-4

螺旋流动长度
Spiral flow length cm Internal Method

机械性能
MECHANICAL Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

球压硬度(H 961/30)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位
UNIT 测试方法
TEST METHOD

温度指数(50% 拉伸强度损失，20000 hr)
Temperature index ℃ IEC 216

温度指数(50% 拉伸强度损失，5000 hr)
Temperature index ℃ IEC 216

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(8.0 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/C

熔融温度
Melting temperature ℃ DIN EN 11357-1

熔融温度(DSC)
Melting temperature ℃ ISO 3146

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

燃烧速率(1 mm)
Burning rate mm/min FMVSS 302

补充信息
Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位
UNIT 测试方法
TEST METHOD

灰份含量
Ash Content % ISO 1172

加工方式

注射 Ultramid® B3WG10 BK00564 AKROMID® B3 GF 50 1 natural (2531) 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

注射速度

备注

1 一般属性：这些不能被视为规格。

2 模具温度: 176°F, 熔体温度: 518°F, 注塑压力: 1.09E+4 psi

3 cross section of flow spiral: 7 mm x 3.5 mm

4 0.079 in/min

5 10°C/min

6 >1 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注
返回顶部

PA6，Ultramid® B3WG10 BK00564对比PA6，AKROMID® B3 GF 50 1 natural (2531)对比物性表,价格行情_搜料_soliao