PPS，Fortron® 1130L4 FC对比PPS，Fortron® 1130L4物性表,价格行情_搜料

牌号信息	Fortron® 1130L4 FC 物性表 PPS & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	Fortron® 1130L4 物性表 PPS & 美国塞拉尼斯指导价格：暂无塑料库存： 96800kg
牌号简介	Fortron® 1130L4 FC是一种30%玻璃纤维增强PPS，具有优异的耐热性和耐化学性，可用于食品接触应用。它本身具有阻燃性，硬度高，强度和刚度平衡良好。特别适用于需要较长流动长度的薄壁零件。由于填料含量低，该等级在二次操作中也表现出良好的可焊性。 Fortron 1130L4FC is a 30% glass-reinforced PPS that has excellent heat and chemical resistance for use in food contact applications. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.	Fortron® 1130L4是一种30%的玻璃纤维增强聚苯硫醚，具有优异的耐热性和耐化学性。它本身具有阻燃性，硬度高，强度和刚度平衡良好。特别适用于需要较长流动长度的薄壁零件。由于填料含量低，该等级在二次操作中也表现出良好的可焊性。 Fortron 1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.

产品描述
厂家：	美国塞拉尼斯 Celanese	美国塞拉尼斯 Celanese
类别：	PPS PPS	PPS PPS
填料：	玻璃纤维 30	玻璃纤维 30
用途：	薄壁部件,非特定食品应用	薄壁部件
性能特点：	机械强度好,硬度高,阻燃,食品接触,耐高温,耐化学性,焊接,防火阻燃等级V-0 Good Rigidity,Good Hardness,Flame Characteristics,Food contact compliance,High Heat Resistance,Solvent resistance,Welding,V-0	机械强度好,硬度高,阻燃,耐高温,耐化学性,焊接,防火阻燃等级V-0 Good Rigidity,Good Hardness,Flame Characteristics,High Heat Resistance,Solvent resistance,Welding,V-0
加工条件：

技术参数

物理性能
PHYSICAL Fortron® 1130L4 FC Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD)
Shrinkage rate % ISO 294-4

特定体积
Specific volume cm³/g ASTM D792

冲击性能
IMPACT Fortron® 1130L4 FC Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Fortron® 1130L4 FC Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

玻璃化转变温度
Glass transition temperature ℃ ISO 11357-2

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Fortron® 1130L4 FC Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257

体积电阻率
Volume resistivity ohms·cm IEC 60093

体积电阻率(--)
Volume resistivity ohms·cm ASTM D257

体积电阻率(--)
Volume resistivity ohms·cm IEC 60093

相比漏电起痕指数
Compared to the leakage tracing index V ASTM D3638

耐电弧性
Arc resistance sec ASTM D495

耗散因数(1 kHz)
Dissipation factor ASTM D150

耗散因数(1 MHz)
Dissipation factor ASTM D150

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Fortron® 1130L4 FC Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.50 mm)
Flame retardant level UL 94

补充信息
Fortron® 1130L4 FC Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

Specimen Thickness(Shrinkage)
Specimen Thickness（Shrinkage） mm Internal Method

Specimen Thickness(Shrinkage)
Specimen Thickness（Shrinkage） mm 内部方法

机械性能
MECHANICAL Fortron® 1130L4 FC Fortron® 1130L4 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ISO 527-2/1A/5

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/1A/5

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

洛氏硬度(M 级)
Rockwell hardness ASTM D785

洛氏硬度(M 级)
Rockwell hardness ISO 2039-2

加工方式

注射 Fortron® 1130L4 FC Fortron® 1130L4 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

注射速度 Fortron® 1130L4 FC Fortron® 1130L4 单位测试方法

保压 MPa

背压 MPa

备注

2 Break

3 10°C/min

1 一般属性：这些不能被视为规格。

2 Break

3 10°C/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
机械性能
加工方式
注射
注射速度
备注
返回顶部

PPS，Fortron® 1130L4 FC对比PPS，Fortron® 1130L4对比物性表,价格行情_搜料_soliao