POM共聚，Ultraform® N 2640 Z2 UNC Q600对比POM共聚，Ultraform® N 2310 P Q600物性表,价格行情_搜料

牌号信息	Ultraform® N 2640 Z2 UNC Q600 物性表 POM共聚 & 德国巴斯夫指导价格：暂无塑料库存：缺货	Ultraform® N 2310 P Q600 物性表 POM共聚 & 德国巴斯夫指导价格：暂无塑料库存：缺货
牌号简介	Ultraform® N 2640 Z2 UNC Q600是一种弹性体改性注塑POM级，具有高冲击强度。典型应用包括玩具部件，如自行车框架、汽车部件，如覆盖件和挡风玻璃雨刷器单元、夹子、卡扣和紧固件以及其他受到冲击应力的部件。 Ultraform N 2640 Z2 UNC Q600 is an elastomer-modified injection molding POM grade with high impact strength. Applications Typical applications include toys components such as bicycle frames, automotive parts such as cladding elements and windshield wiper units, and clips, snap and fastening elements, and other components subject to impact stress.	Ultraform® N 2310 P Q600是一种通用注塑POM级，含有特殊润滑剂。摩擦系数低，磨损极低，机械性能不变。典型应用包括弹簧元件、夹子、齿轮和其他需要低摩擦和磨损的应用。 Ultraform N 2310 P Q600 is a general-purpose injection molding POM grade containing special lubricant. Low frictional coefficient giving extremely low wear with otherwise unaltered mechanical properties. Applications Typical applications include spring elements, clips, gears and other applications requiring low friction and wear.

产品描述
厂家：	德国巴斯夫 BASF	德国巴斯夫 BASF
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：
用途：	玩具,紧固件,汽车外部零件	通用,齿轮,弹簧
性能特点：	冲击性能好,共聚物 High impact resistance,Copolymer	低摩擦系数,润滑性,共聚物,耐磨 Low coefficient of friction,Lubricating,Copolymer,Good wear resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Ultraform® N 2640 Z2 UNC Q600 Ultraform® N 2310 P Q600 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，50% RH)
Water absorption rate % ASTM D570

吸水率(饱和)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD)
Shrinkage rate % ISO 294-4

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

机械性能
MECHANICAL Ultraform® N 2640 Z2 UNC Q600 Ultraform® N 2310 P Q600 单位
UNIT 测试方法
TEST METHOD

Tensile Creep Modulus(1 hr)
Tensile Creep Modulus（1 hr） MPa ISO 899-1

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(屈服，23℃)
Tensile strain % ASTM D638

拉伸应变(屈服，23℃)
Tensile strain % ISO 527-2

拉伸强度(屈服，-40℃)
tensile strength MPa ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

拉伸蠕变模量(1000 hr)
Tensile creep modulus MPa ISO 899-1

标称拉伸断裂应变(23℃)
Nominal tensile fracture strain % ISO 527-2

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT Ultraform® N 2640 Z2 UNC Q600 Ultraform® N 2310 P Q600 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL Ultraform® N 2640 Z2 UNC Q600 Ultraform® N 2310 P Q600 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度(DSC)
Melting temperature ℃ ISO 3146

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ASTM E831

电气性能
ELECTRICAL Ultraform® N 2640 Z2 UNC Q600 Ultraform® N 2310 P Q600 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant IEC 60250

介电常数(100 Hz)
Dielectric constant IEC 60250

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率(1.50 mm)
Volume resistivity ohms·cm ASTM D257

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms ASTM D257

表面电阻率
Surface resistivity ohms IEC 60093

加工方式

注射 Ultraform® N 2640 Z2 UNC Q600 Ultraform® N 2310 P Q600 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

模具温度 °C

注塑压力 MPa

备注

1 一般属性：这些不能被视为规格。

2 1.5 mm

1 一般属性：这些不能被视为规格。

2 1.5 mm


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
加工方式
注射
备注