POM共聚，Hostaform® M10AE对比POM共聚，Ultraform® E3120 BM物性表,价格行情_搜料

牌号信息	Hostaform® M10AE 物性表 POM共聚 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货	Ultraform® E3120 BM 物性表 POM共聚 & 德国巴斯夫指导价格：暂无塑料库存：缺货
牌号简介	聚甲醛共聚物，流动性强，熔融强度高，对溶剂、燃料、强碱有良好的耐化学性，抗水解性好，耐热氧化降解性强。根据21 CFR 177.2470燃烧速率ISO 3795和厚度大于1 mm的FMVSS 302<100 mm/min，单体和添加剂列在欧盟法规（EU）10/2011 FDA中。应用范围：用于挤出吹塑，以及注射成型厚壁，无空隙的成型零件。 POM copolymer Stiff-flowing type with high melt strength; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: For extrusion blow molding, and for injection molding thick-walled, void-free molded parts.	具有高熔融强度、刚度和高拉伸性的材料，用于生产挤压吹塑空心物体。 Material with high melt strength, -stiffness and high stretchability for producing extrusion blow-molded hollow objects.

产品描述
厂家：	美国塞拉尼斯 Celanese	德国巴斯夫 BASF
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：
用途：	厚壁配件（部件）,吹塑成型应用	吹塑成型应用
性能特点：	耐碱,耐水解,熔体强度好,耐化学性,耐燃油 Alkali resistant,Hydrolysis stability,Good melt strength,Solvent resistance,Fuel resistance	机械强度好,熔体强度好,拉伸性能好,共聚物,防火阻燃等级HB Good Rigidity,Good melt strength,Good Tensile Strength,Copolymer,HB
加工条件：	吹塑成型	吹塑成型

技术参数

物理性能
PHYSICAL Hostaform® M10AE Ultraform® E3120 BM 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

熔体体积流动速率(190℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

表观密度
Apparent density g/cm³

机械性能
MECHANICAL Hostaform® M10AE Ultraform® E3120 BM 单位
UNIT 测试方法
TEST METHOD

Tensile Creep Modulus(1 hr)
Tensile Creep Modulus（1 hr） MPa ISO 899-1

拉伸应变(屈服)
Tensile strain % ISO 527-2/1A/50

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/1A/50

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2/1A/1

拉伸蠕变模量(1000 hr)
Tensile creep modulus MPa ISO 899-1

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2/1A/50

标称拉伸断裂应变
Nominal tensile fracture strain % ISO 527-2/50

球压硬度(H358/30)
Ball hardness MPa ISO 2039-1

冲击性能
IMPACT Hostaform® M10AE Ultraform® E3120 BM 单位
UNIT 测试方法
TEST METHOD

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃，局部断裂)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Hostaform® M10AE Ultraform® E3120 BM 单位
UNIT 测试方法
TEST METHOD

最高使用温度(short cycle operation)
Maximum operating temperature ℃

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~55℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

电气性能
ELECTRICAL Hostaform® M10AE Ultraform® E3120 BM 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm IEC 60243-1

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率(1 MHz)
Relative permittivity IEC 60250

相对电容率(100 Hz)
Relative permittivity IEC 60250

相比漏电起痕指数
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

耗散因数(1 MHz)
Dissipation factor IEC 60250

耗散因数(100 Hz)
Dissipation factor IEC 60250

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Hostaform® M10AE Ultraform® E3120 BM 单位
UNIT 测试方法
TEST METHOD

1.60 mm
1.60 mm UL 94

补充信息
Hostaform® M10AE Ultraform® E3120 BM 单位
UNIT 测试方法
TEST METHOD

ISO Type
ISO Type ISO 9988-1

加工方式

注射 Hostaform® M10AE Ultraform® E3120 BM 单位测试方法

保压 MPa

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

注塑压力 MPa

注射速度

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 10°C/min

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
补充信息
加工方式
注射
备注