PA6，CPI PA6 40 Other对比PA6，LNP™ THERMOCOMP™ PF008QS compound物性表,价格行情_搜料

牌号信息	CPI PA6 40 Other 物性表 PA6 & 美国CPI 指导价格：暂无塑料库存：缺货	LNP™ THERMOCOMP™ PF008QS compound 物性表 PA6 & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	尼龙作为一种玻璃填充产品在CPI-Binani D-LFT工艺中工作得很好。它提供了更好的抗冲击性，弹性和弹性，同时创造了一个美好的成品，一个愉快的完成。尼龙比聚丙烯重一些，这可能是为您的产品选择材料时要考虑的一个因素。CPI Binani的工程人员可以根据您完成的产品需求文档（PRD）提供更多信息。 Nylon works very well as a glass filled product in the CPI Binani D-LFT process. It offers improved resistance to impact, modulus, and flex while creating a nice finished product with a pleasant finish. Nylon is somewhat heavier than polypropylene which may be a consideration when selecting materials for your product. The engineering staff at CPI Binani can provide additional information based on your completed Product Requirements Document (PRD)	LNP ThermocompPF008QS是一种基于尼龙6树脂的化合物，含有40%的玻璃纤维。这种材料的附加特性包括：热稳定，减少水分。也称为：lnpThermocomp化合物PF-1008 hs rm产品再订购名称：pf008qs LNP THERMOCOMP PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture.

产品描述
厂家：	美国CPI	沙特沙伯基础 SABIC
类别：	PA6 PA6	PA6 PA6
填料：	玻璃纤维 40	玻璃纤维 40
用途：
性能特点：		热稳定性好 Heat Stabilized
加工条件：		注射成型 Injection Molding

技术参数

机械性能
MECHANICAL CPI PA6 40 Other LNP™ THERMOCOMP™ PF008QS compound 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

泊松比
Poisson's ratio

冲击性能
IMPACT CPI PA6 40 Other LNP™ THERMOCOMP™ PF008QS compound 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch J/m

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

物理性能
PHYSICAL CPI PA6 40 Other LNP™ THERMOCOMP™ PF008QS compound 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

热性能
THERMAL CPI PA6 40 Other LNP™ THERMOCOMP™ PF008QS compound 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

加工方式

注射 CPI PA6 40 Other LNP™ THERMOCOMP™ PF008QS compound 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2,0 in/min

3 80*10*4

4 80*10*4 mm