技术参数
冲击性能 IMPACT
Fortron® 6165A4
Ryton® R-7-120NA
单位 UNIT
测试方法 TEST METHOD
悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam
kJ/m²
ISO 180/1U
悬臂梁无缺口冲击强度(3.2 mm)
Notched impact strength of cantilever beam
J/m
ASTM D4812
悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch
J/m
ASTM D256
简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
热性能 THERMAL
Fortron® 6165A4
Ryton® R-7-120NA
单位 UNIT
测试方法 TEST METHOD
UL温度额定值
UL temperature rating
℃
UL 746B
导热系数
Thermal conductivity coefficient
W/m/K
热变形温度(0.45 MPa,退火)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃
ASTM D648
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/A
热变形温度(8.0 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/C
熔融温度
Melting temperature
℃
ISO 11357-3
玻璃化转变温度
Glass transition temperature
℃
ISO 11357-2
线性热膨胀系数(-50 到 50℃)
Linear coefficient of thermal expansion
cm/cm/℃
ASTM E831
线性热膨胀系数(100 到 200℃)
Linear coefficient of thermal expansion
cm/cm/℃
ASTM E831
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
ASTM E831
线性热膨胀系数(TD)
Linear coefficient of thermal expansion
1/℃
ISO 11359-2
线性热膨胀系数(TD)
Linear coefficient of thermal expansion
ASTM E831
电气性能 ELECTRICAL
Fortron® 6165A4
Ryton® R-7-120NA
单位 UNIT
测试方法 TEST METHOD
介电常数(1 kHz)
Dielectric constant
ASTM D150
介电常数(1 MHz)
Dielectric constant
ASTM D150
介电常数(25 ℃,1 kHz)
Dielectric constant
ASTM D150
介电常数(25 ℃,1 MHz)
Dielectric constant
ASTM D150
介电强度
Dielectric strength
kV/mm
ASTM D149
介电强度
Dielectric strength
kV/mm
IEC 60243-1
体积电阻率
Volume resistivity
ohms·cm
ASTM D257
体积电阻率
Volume resistivity
ohms·cm
IEC 60093
相对电容率(1 MHz)
Relative permittivity
IEC 60250
相比漏电起痕指数
Compared to the leakage tracing index
V
IEC 60112
相比漏电起痕指数
Compared to the leakage tracing index
V
UL 746
绝缘电阻(90℃)
insulation resistance
ohms
耐电弧性
Arc resistance
sec
ASTM D495
耗散因数(1 kHz)
Dissipation factor
ASTM D150
耗散因数(1 MHz)
Dissipation factor
ASTM D150
耗散因数(1 MHz)
Dissipation factor
IEC 60250
耗散因数(25℃,1 kHz)
Dissipation factor
ASTM D150
耗散因数(25℃,1 MHz)
Dissipation factor
ASTM D150
表面电阻率
Surface resistivity
ohms
ASTM D257
表面电阻率
Surface resistivity
ohms
IEC 60093
阻燃性能 FLAMMABILITY
Fortron® 6165A4
Ryton® R-7-120NA
单位 UNIT
测试方法 TEST METHOD
1.60 mm
1.60 mm
UL 94
极限氧指数
Extreme oxygen index
%
ASTM D2863
极限氧指数
Extreme oxygen index
%
ISO 4589-2
阻燃等级(0.75 mm)
Flame retardant level
UL 94
阻燃等级(1.50 mm)
Flame retardant level
UL 94
阻燃等级(3.00 mm)
Flame retardant level
UL 94
补充信息
Fortron® 6165A4
Ryton® R-7-120NA
单位 UNIT
测试方法 TEST METHOD
Specimen Thickness(Shrinkage)
Specimen Thickness(Shrinkage)
mm
Internal Method
机械性能 MECHANICAL
Fortron® 6165A4
Ryton® R-7-120NA
单位 UNIT
测试方法 TEST METHOD
压缩强度
compressive strength
MPa
ASTM D695
弯曲强度
bending strength
MPa
ASTM D790
弯曲强度
bending strength
MPa
ISO 178
弯曲模量
Bending modulus
MPa
ASTM D790
弯曲模量
Bending modulus
MPa
ISO 178
弯曲模量(23℃)
Bending modulus
MPa
ISO 178
拉伸应变(断裂)
Tensile strain
%
ASTM D638
拉伸应变(断裂)
Tensile strain
%
ISO 527-2
拉伸应变(断裂)
Tensile strain
%
ISO 527-2/1A/5
拉伸应变(断裂,23℃)
Tensile strain
%
ASTM D638
拉伸强度
tensile strength
MPa
ASTM D638
拉伸强度
tensile strength
MPa
ISO 527-2
拉伸强度(断裂)
tensile strength
MPa
ISO 527-2/1A/5
拉伸强度(断裂,23℃)
tensile strength
MPa
ASTM D638
拉伸模量
Tensile modulus
MPa
ISO 527-2/1A/1
泊松比
Poisson's ratio
ISO 527
洛氏硬度(M 级)
Rockwell hardness
ASTM D785
洛氏硬度(M 级)
Rockwell hardness
ISO 2039-2
洛氏硬度(R 级)
Rockwell hardness
ASTM D785
物理性能 PHYSICAL
Fortron® 6165A4
Ryton® R-7-120NA
单位 UNIT
测试方法 TEST METHOD
Specific Heat Capacity of Melt
Specific Heat Capacity of Melt
J/kg/℃
Internal Method
吸水率(23℃,24hr)
Water absorption rate
%
ASTM D570
吸水率(饱和,23℃)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ASTM D792
密度
Density
g/cm³
ISO 1183
收缩率(MD)
Shrinkage rate
%
ASTM D955
收缩率(MD)
Shrinkage rate
%
ISO 294-4
收缩率(MD:3.2 mm)
Shrinkage rate
%
收缩率(TD)
Shrinkage rate
%
ASTM D955
收缩率(TD)
Shrinkage rate
%
ISO 294-4
收缩率(TD:3.2 mm)
Shrinkage rate
%
熔体质量流动速率
Melt Flow Rate
g/10min
ASTM D1238
特定体积
Specific volume
cm³/g
ASTM D792
螺旋流动长度
Spiral flow length
Internal Method