PP均聚，YUPLENE® BX3900对比PP均聚，Polifor® 3 NATURALE物性表,价格行情_搜料

牌号信息	YUPLENE® BX3900 物性表 PP均聚 & 韩国SK化学指导价格：12889.0元/吨塑料库存： 5000kg	Polifor® 3 NATURALE 物性表 PP均聚 & 美国塞拉尼斯指导价格：暂无塑料库存：缺货
牌号简介	YUPLENE BX3900是一种高结晶丙烯抗冲共聚物，专为注塑应用而设计。YUPLENE BX3900在刚度、流动性、机械性能、耐热性和冲击强度等方面具有优异的性能，使其适用于汽车零部件、电器、大型容器、薄壁和超高速注塑应用。这不是化学开裂等级，因此没有表面气体痕迹。YUPLENE BX3900可减少各种注塑问题，如表面问题、收缩、翘曲等，并因快速结晶而缩短注塑周期。 Y UPLENE BX3900 is a high crystalline propylene impact copolymer designed for injection molding applications. YUPLENE BX3900 has excellent properties in stiffness, flow, mechanical properties, heat resistance and impact strength, which make YUPLENE BX3900 suitable for auto parts, electric appliances, large size containers, thin wall and very high speed injection applications. This is not a chemical cracked grade so it is free from surface gas mark. YUPLENE BX3900 can reduce various injection problems such as surface trouble, shrink, warpage etc. and reduce the cycle time of injection molding due to rapid crystallization. Application: Injection Molding / automobile applications, industrial parts for electronic, large container Characteristics: High Stiffness, High Impact Strength	聚丙烯均聚物 Polypropylene homopolymer

产品描述
厂家：	韩国SK化学 SKC	美国塞拉尼斯 Celanese
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：	汽车外部零件,薄壁部件
性能特点：	耐热性好,高刚性 Heat Resistance, Good	均聚物,防火阻燃等级HB Homopolymer,HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL YUPLENE® BX3900 Polifor® 3 NATURALE 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率
Shrinkage rate % 内部方法

熔体质量流动速率
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

螺旋流动长度
Spiral flow length mm 内部方法

热性能
THERMAL YUPLENE® BX3900 Polifor® 3 NATURALE 单位
UNIT 测试方法
TEST METHOD

热变形温度
Hot deformation temperature ℃ ASTM D648

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 2

机械性能
MECHANICAL YUPLENE® BX3900 Polifor® 3 NATURALE 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus kg/cm² ASTM D790

弯曲模量
Bending modulus MPa ASTM D790

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength kg/cm² ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

冲击性能
IMPACT YUPLENE® BX3900 Polifor® 3 NATURALE 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kg.cm/cm ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kg.cm/cm ASTM D256

老化性能
AGING YUPLENE® BX3900 Polifor® 3 NATURALE 单位
UNIT 测试方法
TEST METHOD

加速烘箱老化(150°C)
Accelerate oven aging hr ASTM D3012

阻燃性能
FLAMMABILITY YUPLENE® BX3900 Polifor® 3 NATURALE 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.20 mm)
Flame retardant level UL 94

加工方式

注射 YUPLENE® BX3900 Polifor® 3 NATURALE 单位测试方法

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 速率 A (50°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
热性能
机械性能
冲击性能
老化性能
阻燃性能
加工方式
注射
备注
返回顶部

PP均聚，YUPLENE® BX3900对比PP均聚，Polifor® 3 NATURALE对比物性表,价格行情_搜料_soliao