技术参数
物理性能
PHYSICAL
Delrin® 100 BK602
Delrin® 100 NC010
单位
UNIT
测试方法
TEST METHOD
Specific Heat Capacity of Melt
Specific Heat Capacity of Melt
J/kg/℃
吸水率(平衡,23℃,50% RH,2.00 mm)
Water absorption rate
%
ISO 62
吸水率(饱和,23℃,2.00 mm)
Water absorption rate
%
ISO 62
密度
Density
g/cm³
ISO 1183
密度 Density
Density
g/cm³
ISO 1183
成型收缩率 Molding Shrinkage(横向流动 Across flow)
Molding shrinkage
%
ISO 294-4
成型收缩率 Molding Shrinkage(流动 flow)
Molding shrinkage
%
ISO 294-4
收缩率(MD)
Shrinkage rate
%
ISO 294-4
收缩率(TD)
Shrinkage rate
%
ISO 294-4
熔体体积流动速率 Melt Volume Rate
Melt Volume Rate
cm³/10min
ISO 1133
熔体体积流动速率(190℃,2.16 kg)
Melt Volume Rate
cm³/10min
ISO 1133
熔体密度
Melt density
g/cm³
熔体密度 Melt Density
Melt Density
g/cm³
熔体质量流动速率
Melt Flow Rate
g/10min
ISO 1133
熔体质量流动速率 Melt Flow Rate(190℃,2.16kg)
Melt Flow Rate
g/10min
ISO 1133
机械性能
MECHANICAL
Delrin® 100 BK602
Delrin® 100 NC010
单位
UNIT
测试方法
TEST METHOD
Tensile Creep Modulus(1 hr)
Tensile Creep Modulus(1 hr)
MPa
ISO 899-1
压缩强度
compressive strength
MPa
ISO 604
弯曲强度(3.50% 应变)
bending strength
MPa
ISO 178
弯曲模量
Bending modulus
MPa
ISO 178
弯曲模量 Flexural Modulus
Flexural Modulus
MPa
ISO 178
拉伸伸长率 Tensile Elongation(屈服 yld)
Tensile Elongation
%
ISO 527-2
拉伸应变 Tensile Strain(断裂 brk)
Tensile Strain
%
ISO 527
拉伸应变(屈服)
Tensile strain
%
ISO 527-2
拉伸强度 Tensile Strength(屈服 yld)
Tensile Strength
MPa
ISO 527-2
拉伸强度(屈服)
tensile strength
MPa
ISO 527-2
拉伸模量
Tensile modulus
MPa
ISO 527-2
拉伸模量 Tensile Modulus(-)
Tensile Modulus
MPa
ISO 527
拉伸蠕变模量(1000 hr)
Tensile creep modulus
MPa
ISO 899-1
标称拉伸断裂应变
Nominal tensile fracture strain
%
ISO 527-2
泊松比 Poisson's Ratio
Poisson's Ratio
ASTM E132
洛氏硬度 Rockwell Hardness(M)
Rockwell hardness
ISO 2039-2
洛氏硬度 Rockwell Hardness(R)
Rockwell hardness
ISO 2039-2
洛氏硬度(M 级)
Rockwell hardness
ISO 2039-2
洛氏硬度(R 级)
Rockwell hardness
ISO 2039-2
冲击性能
IMPACT
Delrin® 100 BK602
Delrin® 100 NC010
单位
UNIT
测试方法
TEST METHOD
悬臂梁缺口冲击强度 Izod Notched Impact strength(-40℃)
Izod Notched Impact strength
KJ/m²
ISO 180/1A
悬臂梁缺口冲击强度 Izod Notched Impact strength(23℃)
Izod Notched Impact strength
KJ/m²
ISO 180/1A
悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch
kJ/m²
ISO 180-1A
简支梁无缺口冲击强度 Charpy Unnotched Impact strength(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度 Charpy Unnotched Impact strength(23℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength
kJ/m²
ISO 179/1eU
简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength
ISO 179/1eU
简支梁缺口冲击强度 Charpy notched Impact strength(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度 Charpy notched Impact strength(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength
kJ/m²
ISO 179/1eA
热性能
THERMAL
Delrin® 100 BK602
Delrin® 100 NC010
单位
UNIT
测试方法
TEST METHOD
Effective Thermal Diffusivity
Effective Thermal Diffusivity
m²/s
热变形温度 HDT(1.8 MPa)
Hot deformation temperature HDT
℃
ISO 75-1/-2
热变形温度(0.45 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/B
热变形温度(1.8 MPa,未退火)
Hot deformation temperature
℃
ISO 75-2/A
熔融温度
Melting temperature
℃
ISO 11357-3
熔融温度 Melting temperature
Melting temperature
℃
ISO 11357-3
线性热膨胀系数 Coeff.of linear therm expansion(横向 Transverse)
Coeff. of linear thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数 Coeff.of linear therm expansion(横向 Transverse:-40℃-23℃)
Coeff. of linear thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数 Coeff.of linear therm expansion(流动 flow)
Coeff. of linear thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数 Coeff.of linear therm expansion(流动 flow:-40℃-23℃)
Coeff. of linear thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数(--)
Linear coefficient of thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数(-40 到 23℃)
Linear coefficient of thermal expansion
cm/cm/℃
ISO 11359-2
线性热膨胀系数(MD)
Linear coefficient of thermal expansion
ISO 11359-2
线性热膨胀系数(TD)
Linear coefficient of thermal expansion
ISO 11359-2
维卡软化温度(A50)
Vicat Softening Temp
℃
ISO 306/A50
维卡软化温度(B50)
Vicat Softening Temp
℃
ISO 306
退火时间 Annealing time
Annealing time
min/mm
退火时间(Optional)
annealing time
min/mm
退火温度
annealing temperature
℃
退火温度 Annealing Temperature
Annealing Temperature
℃
电气性能
ELECTRICAL
Delrin® 100 BK602
Delrin® 100 NC010
单位
UNIT
测试方法
TEST METHOD
介电常数 Dielectric Constant(100Hz)
Dielectric Constant
IEC 62631-2-1
介电常数 Dielectric Constant(1MHz)
Dielectric Constant
IEC 62631-2-1
介电强度
Dielectric strength
kV/mm
IEC 60243-1
介电强度 Dielectric Strength
Dielectric Strength
kV/mm
IEC 60243-1
体积电阻率
Volume resistivity
ohms·cm
IEC 60093
体积电阻率 Volume Resistivity
Volume Resistance
ohms·cm
IEC 60093
相对电容率(1 MHz)
Relative permittivity
IEC 60250
相对电容率(100 Hz)
Relative permittivity
IEC 60250
相比漏电起痕指数
Compared to the leakage tracing index
V
IEC 60112
相比漏电起痕指数 Comparative Tracking Index
Compared Tracking Index
V
IEC 60112
耗散因数 Dissipation Factor(100Hz)
Dissipation Factor
IEC 62631-2-1
耗散因数 Dissipation Factor(1MHz)
Dissipation Factor
IEC 62631-2-1
耗散因数(1 MHz)
Dissipation factor
IEC 60250
耗散因数(100 Hz)
Dissipation factor
IEC 60250
表面电阻率
Surface resistivity
ohms
IEC 60093
表面电阻率 Surface Resistivity
Surface Resistivity
ohms
IEC 60093
阻燃性能
FLAMMABILITY
Delrin® 100 BK602
Delrin® 100 NC010
单位
UNIT
测试方法
TEST METHOD
FMVSS 阻燃等级
FMVSS flame retardant rating
FMVSS 302
FMVSS 阻燃等级
FMVSS flame retardant rating
FMVSS 302
可燃性等级(0.8 mm)
Flammability level
IEC 60695-11-10, -20
可燃性等级(1.5 mm)
Flammability level
IEC 60695-11-10, -20
燃烧速率(1 mm)
Burning rate
mm/min
ISO 3795
阻燃等级 Flame Class Rating(0.8 mm)
Flame Class Rating
UL 94
阻燃等级 Flame Class Rating(1.00 mm³)
Flame Class Rating
mm/min
ISO 3795
阻燃等级 Flame Class Rating(1.5 mm )
Flame Class Rating
UL 94
阻燃等级(0.80 mm)
Flame retardant level
UL 94
阻燃等级(1.50 mm)
Flame retardant level
UL 94
雾化(F-value(refraction))
atomization
%
ISO 6452
雾化(G-value(condensate))
atomization
g
ISO 6452
补充信息
Delrin® 100 BK602
Delrin® 100 NC010
单位
UNIT
测试方法
TEST METHOD
排放
discharge
mg/kg
VDA 275
有机化合物的排放
Emissions of organic compounds
µgC/g
VDA 277