PP均聚，OnForce™ LFT LFT PP-30 LGF/000 1001对比PP均聚，Polytron® P30B11物性表,价格行情_搜料

牌号信息	OnForce™ LFT LFT PP-30 LGF/000 1001 物性表 PP均聚 & 美国普立万指导价格：暂无塑料库存：缺货	Polytron® P30B11 物性表 PP均聚 & 以色列普利朗指导价格：暂无塑料库存：缺货
牌号简介	普立万的长纤维热塑性（LFT）化合物是为要求高硬度和良好冲击的应用而配制的，如金属替换或其他结构应用。与标准短纤维产品相比，这些产品具有更高的物理和机械性能。LFT化合物的好处包括改善冲击强度、弹性模量和材料强度，范围从亚环境到高度升高。此外，与传统的高填充短纤维产品相比，LFT化合物在蠕变和疲劳性能方面提供了改进的性能，提高了尺寸稳定性，并表现出优异的表面光洁度。 PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.	化学耦合30%LGF增强黑色聚丙烯，热稳定注塑应用。 A chemically coupled 30% LGF reinforced black PP, heat stabilized for injection moulding applications.

产品描述
厂家：	美国普立万 Polyone	以色列普利朗 Ram-On
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：	长纤维填料 30	长纤维填料 30
用途：
性能特点：		化学耦合,热稳定性好,防火阻燃等级HB Chemical coupling,Heat Stabilized,HB
加工条件：		注射成型 Injection Molding

技术参数

物理性能
PHYSICAL OnForce™ LFT LFT PP-30 LGF/000 1001 Polytron® P30B11 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate % ASTM D955

机械性能
MECHANICAL OnForce™ LFT LFT PP-30 LGF/000 1001 Polytron® P30B11 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-2

冲击性能
IMPACT OnForce™ LFT LFT PP-30 LGF/000 1001 Polytron® P30B11 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179

热性能
THERMAL OnForce™ LFT LFT PP-30 LGF/000 1001 Polytron® P30B11 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融峰值温度
Melting peak temperature ℃ ASTM D3418

熔融温度
Melting temperature ℃ ISO 11357-3

阻燃性能
FLAMMABILITY OnForce™ LFT LFT PP-30 LGF/000 1001 Polytron® P30B11 单位
UNIT 测试方法
TEST METHOD

3.00 mm
3.00 mm UL 94

FMVSS Flammability(2.00 mm)
FMVSS Flammability（2.00 mm） mm/min FMVSS 302

灼热丝可燃性指数
Glowing wire flammability index ℃ IEC 60695-2-12

加工方式

注射 OnForce™ LFT LFT PP-30 LGF/000 1001 Polytron® P30B11 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
备注