PS(HIPS)，Avantra® 8330对比PS(HIPS)，TOTAL Polystyrene Impact 5240物性表,价格行情_搜料

牌号信息	Avantra® 8330 物性表 PS(HIPS) & 美国PMC 指导价格：暂无塑料库存：缺货	TOTAL Polystyrene Impact 5240 物性表 PS(HIPS) & 法国道达尔指导价格：暂无塑料库存：缺货
牌号简介	Avantra® 8330是一种高抗冲击聚苯乙烯的阻燃等级，具有无与伦比的耐热性、高刚度和热稳定性。它不含多溴二苯醚，符合UL94V-2（0.057“-0.110”/1.45 mm-2.8 mm）额定值。应用：Avantra® 8330主要用于复印机部件、商用机器外壳和电器部件。 Avantra® 8330 is a ignition resistant grade of high impact polystyrene offering unmatched heat resistance, high stiffness and thermal stability. It is free of polybrominated diphenylethers and meets UL94V-2 (0.057"-0.110"/1.45 mm - 2.8mm) rating. Applications: Avantra® 8330 is intended primarily for copier parts, business machine enclosures, and appliance components.	聚苯乙烯冲击5240是高耐热，高冲击聚苯乙烯挤出和注射应用。要求高耐热性和高冲击性的应用。热灌装、配制、剃须刀 POLYSTYRENE IMPACT 5240 is high heat resistant, high impact polystyrene for extrusion and injection applications. Applications Applications which require high heat resistance coupled with high impact. Hot fill, compounding, razors

产品描述
厂家：	美国PMC	法国道达尔 TOTAL
类别：	PS(HIPS) PS (HIPS)	PS(HIPS) PS (HIPS)
填料：
用途：	商务设备,印刷机零件,家电部件	复合
性能特点：	机械强度好,冲击性能好,耐高温,热稳定性好,防火阻燃等级V-2 Good Rigidity,High impact resistance,High Heat Resistance,Heat Stabilized,V-2	冲击性能好,食品接触,耐高温 High impact resistance,Food contact compliance,High Heat Resistance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Avantra® 8330 TOTAL Polystyrene Impact 5240 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50%)
Water absorption rate % ASTM D570

吸水率(饱和，23℃)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率
Shrinkage rate %

收缩率(MD)
Shrinkage rate % ASTM D955

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(200℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

表观密度
Apparent density g/cm³

冲击性能
IMPACT Avantra® 8330 TOTAL Polystyrene Impact 5240 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256-A

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179-1eA

热性能
THERMAL Avantra® 8330 TOTAL Polystyrene Impact 5240 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/A

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

维卡软化温度(A50)
Vicat Softening Temp ℃ ISO 306/A50

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

阻燃性能
FLAMMABILITY Avantra® 8330 TOTAL Polystyrene Impact 5240 单位
UNIT 测试方法
TEST METHOD

阻燃等级(1.60 mm，本色，黑色，固体)
Flame retardant level UL 94

阻燃等级(2.8 mm，本色固体，黑色固体)
Flame retardant level UL 94

机械性能
MECHANICAL Avantra® 8330 TOTAL Polystyrene Impact 5240 单位
UNIT 测试方法
TEST METHOD

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ISO 527-2

洛氏硬度(L 级)
Rockwell hardness ASTM D785

洛氏硬度(R 级)
Rockwell hardness ISO 2039-2

电气性能
ELECTRICAL Avantra® 8330 TOTAL Polystyrene Impact 5240 单位
UNIT 测试方法
TEST METHOD

介电强度
Dielectric strength kV/mm

表面电阻率
Surface resistivity ohms IEC 60093

加工方式

注射 Avantra® 8330 TOTAL Polystyrene Impact 5240 单位测试方法

加工熔体温度 °C

备注

1 一般属性：这些不能被视为规格。

2 方法 I (三点负荷)

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
阻燃性能
机械性能
电气性能
加工方式
注射
备注
返回顶部

PS(HIPS)，Avantra® 8330对比PS(HIPS)，TOTAL Polystyrene Impact 5240对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别