PC，LEXAN™ HFD4271 resin对比PC，LEXAN™ FXE4271L resin物性表,价格行情_搜料

牌号信息	LEXAN™ HFD4271 resin 物性表 PC & 沙特沙伯基础指导价格：56700.0元/吨塑料库存： 12425kg	LEXAN™ FXE4271L resin 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	lexan hfd4271树脂lexan hfd4271是一种10%玻璃填充、高流量、冲击改性、注射成型的等级，设计用于高流量和优越的表面外观。HFD4271具有良好的脱模性、冲击韧性和广阔的色彩空间。 LEXAN HFD4271 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4271 has enhanced mold release, impact ductility and broad color space.	Lexan FXE4271L是一种10%玻璃填充的冲击改性聚碳酸酯，具有优异的遮光性能。它是专为高流量，优越的表面外观，提高释放和良好的冲击韧性。FXE4271L仅提供白色，是遮光板应用的理想选择。 LEXAN FXE4271L is a 10% glass filled, impact modified polycarbonate with excellent light-shield capability. It is designed for high flow, superior surface appearance, enhance release and good impact ductility. FXE4271L is available in white color only and ideal for light-shield applications.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：	玻璃纤维 10	玻璃纤维 10
用途：	电气/电子应用领域,电子显示器	电气/电子应用领域,电子显示器
性能特点：	表面光泽度好,冲击性能好,流动性高,机械强度好-延展,含脱模剂,防火阻燃等级HB Good surface appearance,High impact resistance,High liquidity,Ductility,Good stripping performance,HB	表面光泽度好,冲击性能好,流动性高,含脱模剂 Good surface appearance,High impact resistance,High liquidity,Good stripping performance
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LEXAN™ HFD4271 resin LEXAN™ FXE4271L resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

收缩率(TD：3.2 mm)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LEXAN™ HFD4271 resin LEXAN™ FXE4271L resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain %

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain %

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸模量
Tensile modulus MPa ASTM D638

冲击性能
IMPACT LEXAN™ HFD4271 resin LEXAN™ FXE4271L resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LEXAN™ HFD4271 resin LEXAN™ FXE4271L resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(125℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(强度机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

阻燃性能
FLAMMABILITY LEXAN™ HFD4271 resin LEXAN™ FXE4271L resin 单位
UNIT 测试方法
TEST METHOD

0.40 mm
0.40 mm UL 94

加工方式

注射 LEXAN™ HFD4271 resin LEXAN™ FXE4271L resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

建议注射量 LEXAN™ HFD4271 resin LEXAN™ FXE4271L resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min

5 80*10*3 sp=62mm

6 80*10*3

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.051 in/min


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
阻燃性能
加工方式
注射
建议注射量
备注
返回顶部

PC，LEXAN™ HFD4271 resin对比PC，LEXAN™ FXE4271L resin对比物性表,价格行情_搜料_soliao