CAB，Tenite™ Butyrate 264A3720013 Clear, Trsp对比CAB，Tenite™ Butyrate 285A2R30010 Natural, Trsp物性表,价格行情_搜料

牌号信息	Tenite™ Butyrate 264A3720013 Clear, Trsp 物性表 CAB & 美国伊士曼指导价格：暂无塑料库存：缺货	Tenite™ Butyrate 285A2R30010 Natural, Trsp 物性表 CAB & 美国伊士曼指导价格：暂无塑料库存：缺货
牌号简介	TENITE纤维素塑料以其优良的性能平衡而闻名——韧性、硬度、强度、表面光泽、透明度和温暖感。细纤维素塑料的力学性能随增塑剂用量的不同而不同。增塑剂含量越低，表面越硬，耐热性越高，刚性越高，拉伸强度越高，尺寸稳定性越好。增塑剂含量越高，冲击强度越高。Tenite纤维素塑料有天然、透明、精选的橱柜或烟雾透明和黑色半透明。颜色浓缩物可按10:1到40:1的比例稀释。醋酸丁酸纤维素酯264-13的增塑剂含量为13%。当以特定的FDA颜色编号供应时，它符合FDA对某些食品接触应用的要求。 Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers, or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 264-13 has a plasticizer level of 13%. It meets FDA requirements for certain food-contact applications when supplied in specific FDA color numbers.	TENITE纤维素塑料以其优良的性能平衡而闻名——韧性、硬度、强度、表面光泽、透明度和温暖感。细纤维素塑料的力学性能随增塑剂用量的不同而不同。增塑剂含量越低，表面越硬，耐热性越高，刚性越高，拉伸强度越高，尺寸稳定性越好。增塑剂含量越高，冲击强度越高。Tenite纤维素塑料有天然、透明、精选的琥珀色或烟雾透明和黑色半透明。颜色浓缩物可按10:1到40:1的比例稀释。醋酸丁酸纤维素酯285-10的增塑剂含量为10%，含有防臭面具。 Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulose plastics are available in natural, clear, selected ambers, or smoke transparents and black translucents. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 285-10 has a plasticizer level of 10% and contains an odor mask.

产品描述
厂家：	美国伊士曼 Eastman	美国伊士曼 Eastman
类别：	CAB CAB	CAB CAB
填料：
用途：	体育用品,玩具	把手,医疗/护理用品
性能特点：	机械强度好,透光性好,韧性好,表面光泽度好,可回收,硬度高,食品接触,柔软性好,经增塑 Good Rigidity,Good Clarity,Good flexibility,Good surface appearance,Renewable resources,Good Hardness,Food contact compliance,Soft,Plasticizing	机械强度好,透光性好,韧性好,表面光泽度好,可回收,硬度高,柔软性好,经增塑 Good Rigidity,Good Clarity,Good flexibility,Good surface appearance,Renewable resources,Good Hardness,Soft,Plasticizing
加工条件：

技术参数

物理性能
PHYSICAL Tenite™ Butyrate 264A3720013 Clear, Trsp Tenite™ Butyrate 285A2R30010 Natural, Trsp 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ASTM D570

密度
Density g/cm³ ASTM D792

收缩率(MD)
Shrinkage rate % ASTM D955

冲击性能
IMPACT Tenite™ Butyrate 264A3720013 Clear, Trsp Tenite™ Butyrate 285A2R30010 Natural, Trsp 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-40℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

热性能
THERMAL Tenite™ Butyrate 264A3720013 Clear, Trsp Tenite™ Butyrate 285A2R30010 Natural, Trsp 单位
UNIT 测试方法
TEST METHOD

导热系数(23℃)
Thermal conductivity coefficient W/m/K ASTM C177

比热(23℃)
specific heat J/kg/℃ ASTM C351

比热(23℃)
specific heat J/kg/℃ DSC

热变形温度(0.45 MPa，退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ASTM D648

线性热膨胀系数(MD：23℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

电气性能
ELECTRICAL Tenite™ Butyrate 264A3720013 Clear, Trsp Tenite™ Butyrate 285A2R30010 Natural, Trsp 单位
UNIT 测试方法
TEST METHOD

介电常数(23 ℃，1 MHz)
Dielectric constant ASTM D150

介电强度(23℃)
Dielectric strength kV/mm ASTM D149

耗散因数(23℃，1 MHz)
Dissipation factor ASTM D150

光学性能
OPTICAL Tenite™ Butyrate 264A3720013 Clear, Trsp Tenite™ Butyrate 285A2R30010 Natural, Trsp 单位
UNIT 测试方法
TEST METHOD

折射率
Refractive index ASTM D542

透光率(1520 µm)
Transmittance % ASTM D1003

雾度(1520 µm)
Haze % ASTM D1003

补充信息
Tenite™ Butyrate 264A3720013 Clear, Trsp Tenite™ Butyrate 285A2R30010 Natural, Trsp 单位
UNIT 测试方法
TEST METHOD

加热减量(72 hrs，80℃)
Heating reduction % ASTM D707

可溶性物质损失(23℃)
Loss of soluble substances % ASTM D570

机械性能
MECHANICAL Tenite™ Butyrate 264A3720013 Clear, Trsp Tenite™ Butyrate 285A2R30010 Natural, Trsp 单位
UNIT 测试方法
TEST METHOD

弯曲强度(屈服，23℃)
bending strength MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ASTM D790

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂，23℃)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

备注

1 一般属性：这些不能被视为规格。

2 Conditioned 4 hours at 70°C (158°F)

3 Range: 0.17 to 0.33

1 一般属性：这些不能被视为规格。

2 Conditioned 4 hours at 70°C (158°F)

3 Range: 0.17 to 0.33


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
电气性能
光学性能
补充信息
机械性能
加工方式
备注