PC，LNP™ STAT-KON™ DD200C compound对比PC，LEXAN™ Copolymer CFR5630物性表,价格行情_搜料

牌号信息	LNP™ STAT-KON™ DD200C compound 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货	LEXAN™ Copolymer CFR5630 物性表 PC & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	无聚四氟乙烯聚碳酸酯化合物，具有静电放电安全性和良好的润滑性能，适用于半导体、硬盘驱动器（HDD）和半导体工业。这种材料的附加特性包括：良好的清洁度控制，低LPC，低离子和低排气。 PTFE free polycarbonate compounds with ESD safety and good lubricating perfomrance , suitable for Semiconductor and Hard Disk Drive (HDD) and semicon industry. Added features of this material include: Good cleanliness control, low LPC, low ionic, and low outgassing.	LEXAN？CFR5630聚碳酸酯（PC）是一种非填充树脂，适用于注塑和挤出。这种无氯化、无溴阻燃PC树脂符合FAR25.853烟密度和60秒垂直燃烧和原始设备制造商毒性要求。Lexan CFR5630树脂有透明和不透明两种颜色。 LEXAN? CFR5630 Polycarbonate (PC) is a non-filled resin, suitable for injection molding and extrusion. This non-chlorinated, non-brominated flame retardant PC resin meets FAR25.853 smoke density and 60 second vertical burn and OEM toxicity requirements. LEXAN CFR5630 resin is available in transparent and opaque colors.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PC Polycarbonate	PC Polycarbonate
填料：
用途：	半导体模制化合物	航空航天应用
性能特点：	低离子含量,静电放电保护,低VOC Low (to None) Ion Content,Electrostatic discharge protection,Low odor	低烟,无卤,阻燃,毒性低 Low smoke,Halogen free,Flame Characteristics,Low toxicity
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate %

室外适用性
Outdoor applicability UL 746C

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(MD)
Shrinkage rate %

收缩率(MD：3.2 mm)
Shrinkage rate %

收缩率(TD)
Shrinkage rate %

收缩率(TD：3.2 mm)
Shrinkage rate %

熔体体积流动速率(300℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(300℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ASTM D790

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/5

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/5

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/5

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/5

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam J/m ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam ISO 180/1U

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m²

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/2U

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Be

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(0.45 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

球压测试(123~127℃)
Ball pressure test IEC 60695-10-2

相对温度指数(冲击机械性能)
Relative temperature index ℃ UL 746

相对温度指数(电气性能)
Relative temperature index ℃ UL 746

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度(--)
Vicat Softening Temp ℃ ASTM D1525 10

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

电气性能
ELECTRICAL LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位
UNIT 测试方法
TEST METHOD

介电常数(1.10 GHz)
Dielectric constant ASTM ES7-83

耗散因数(1.1 GHz)
Dissipation factor ASTM ES7-83

表面电阻率
Surface resistivity ohms ASTM D257

静电衰减
Electrostatic attenuation sec FTMS 101B

阻燃性能
FLAMMABILITY LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位
UNIT 测试方法
TEST METHOD

FAA Flammability
FAA Flammability FAR 25.853

NBS烟雾密度(Flaming，Dmax)
NBS smoke density ASTM E662

垂直燃烧测试(a，60s，passes at)
Vertical combustion test sec

垂直燃烧测试(b，12s，passes at)
Vertical combustion test sec

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.0 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

灼热丝起燃温度(1 mm)
Igniting temperature of the hot wire ℃ IEC 60695-2-13

加工方式

注射 LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

注射说明 LNP™ STAT-KON™ DD200C compound LEXAN™ Copolymer CFR5630 单位测试方法

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 0.20 in/min

4 0.079 in/min

5 Yield

6 80*10*4 sp=62mm

7 80*10*4

8 5000V to <50V

2. 50 mm/min

3. 类型 1, 50 mm/min

4. 1.3 mm/min

5. 2.0 mm/min

6. at Yield

7. 80*10*3 sp=62mm

8. 80*10*3 mm

9. 120*10*4 mm

10. 速率 A (50°C/h), 载荷2 (50N)

11. FAR 25.853 A/B


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
注射说明
备注
返回顶部