PA66，NILAMID® A3 W GF30对比PA66，TECHNYL® A 218 V30 BLACK 34 NG物性表,价格行情_搜料

牌号信息	NILAMID® A3 W GF30 物性表 PA66 & 美国塞拉尼斯指导价格：54600.0元/吨塑料库存： 300kg	TECHNYL® A 218 V30 BLACK 34 NG 物性表 PA66 & 德国道默指导价格：暂无塑料库存： 9200kg
牌号简介	NILAMID® A3 W GF30是一种聚酰胺66（尼龙66）化合物，30%玻璃纤维增强，热稳定，UL认证HB。该化合物用于注塑成型。NILAMID® A3 W GF30主要为汽车工业设计。它也适用于电气、电子或工业和消费应用。 NILAMID® A3 W GF30 is a Polyamide 66 (Nylon 66) compound, 30% glass fiber reinforced, heat stabilized, UL listed HB. This compound is intended for injection molding. NILAMID® A3 W GF30 is primarily designed for the Automotive industry. It is also suitable for Electrical and Electronic or Industrial & Consumer applications.	Technyl A 218 V30黑色34 NG是一种聚酰胺66，用30%的玻璃纤维增强，热稳定，用于注塑成型。该产品有黑色可选。 TECHNYL® A 218 V30 Black 34 NG is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. This grade has been specially designed to improve its resistance to automotive cooling liquids, increasing lifetime of parts in permanent contact with such liquids.

产品描述
厂家：	美国塞拉尼斯 Celanese	德国道默 DOMO
类别：	PA66 PA66	PA66 PA66
填料：	玻璃纤维 30	玻璃纤维 30
用途：	工业应用,汽车领域的应用,电气/电子应用领域,消费品应用领域	汽车领域的应用
性能特点：	热稳定性好 Heat Stabilized	热稳定性好,耐乙二醇,防火阻燃等级HB Heat Stabilized,Ethylene glycol,HB
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL NILAMID® A3 W GF30 TECHNYL® A 218 V30 BLACK 34 NG 单位
UNIT 测试方法
TEST METHOD

吸水率(23℃，24hr)
Water absorption rate % ISO 62

吸水率(23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

收缩率(MD)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL NILAMID® A3 W GF30 TECHNYL® A 218 V30 BLACK 34 NG 单位
UNIT 测试方法
TEST METHOD

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(23℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2/1A

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2

拉伸模量(23℃)
Tensile modulus MPa ISO 527-2/1A

热性能
THERMAL NILAMID® A3 W GF30 TECHNYL® A 218 V30 BLACK 34 NG 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Bf

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/Af

热变形温度(1.8 MPa，退火)
Hot deformation temperature ℃ ISO 75-2/Af

熔融温度
Melting temperature ℃ ISO 11357-3

电气性能
ELECTRICAL NILAMID® A3 W GF30 TECHNYL® A 218 V30 BLACK 34 NG 单位
UNIT 测试方法
TEST METHOD

介电强度(2 mm)
Dielectric strength kV/mm IEC 60243-1

体积电阻
Volumetric resistance Ω.cm IEC 60093

体积电阻率
Volume resistivity ohms·cm IEC 60093

相对电容率
Relative permittivity IEC 60250

相比漏电起痕指数(解决方案 A)
Compared to the leakage tracing index V IEC 60112

相比漏电起痕指数(解决方案 B)
Compared to the leakage tracing index V IEC 60112

耗散因数
Dissipation factor IEC 60250

耗散因数(相比漏电起痕指数)
Dissipation factor V IEC 60112

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY NILAMID® A3 W GF30 TECHNYL® A 218 V30 BLACK 34 NG 单位
UNIT 测试方法
TEST METHOD

极限氧指数
Extreme oxygen index % ISO 4589-2

灼热丝可燃性指数(1.6 mm)
Glowing wire flammability index ℃ IEC 60695-2-12

阻燃等级(0.80 mm)
Flame retardant level UL 94

阻燃等级(1.50mm)
Flame retardant level UL-94

阻燃等级(1.60 mm)
Flame retardant level UL 94

阻燃等级(3.00mm)
Flame retardant level UL-94

阻燃等级(3.20 mm)
Flame retardant level UL 94

阻燃等级(极限氧指数)
Flame retardant level % ISO 4589-2

冲击性能
IMPACT NILAMID® A3 W GF30 TECHNYL® A 218 V30 BLACK 34 NG 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1fU

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

加工方式

注射 NILAMID® A3 W GF30 TECHNYL® A 218 V30 BLACK 34 NG 单位测试方法

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

备注

1 一般属性：这些不能被视为规格。

2 20000 hr

1 一般属性：这些不能被视为规格。

2 After ageing in water/glycol for 200 hr at 135°C

3 After ageing in water/glycol for 200 hr at 120°C


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
热性能
电气性能
阻燃性能
冲击性能
加工方式
注射
备注