PUR-脂肪族+TDI，Andur 9000 AP/Curene® 442对比PUR-脂肪族+TDI，Andur 9200 AP/Curene® 442物性表,价格行情_搜料

牌号信息	Andur 9000 AP/Curene® 442 物性表 PUR-脂肪族+TDI & 美国Anderson 指导价格：暂无塑料库存：缺货	Andur 9200 AP/Curene® 442 物性表 PUR-脂肪族+TDI & 美国Anderson 指导价格：暂无塑料库存：缺货
牌号简介	ANDUR 9000-AP是一种以聚醚（PPG）为基础的液体甲苯二异氰酸酯封端预聚物。当用Curene 442[4,4’-亚甲基双（邻氯苯胺）固化该预聚物时，得到硬度为90邵尔A的弹性体。较低硬度的弹性体可通过与各种多元醇反应，并将其与curene 442和其他二胺结合，或通过使用增塑剂获得。 Andur 9000-AP is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 90 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.	andur 9200-ap是一种以聚醚（PPG）为基础的液体、甲苯二异氰酸酯为端接预聚物。当用Curene 442[4,4’-亚甲基双（邻氯苯胺）固化该预聚物时，得到硬度为92邵尔A的弹性体。较低硬度的弹性体可以通过固化和UR 9200-AP与多元醇以及它们与curene 442和其他二胺的结合，或通过使用增塑剂获得。 Andur 9200-AP is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 92 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 9200-AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.

产品描述
厂家：	美国Anderson	美国Anderson
类别：	PUR-脂肪族+TDI PUR-脂肪族+TDI	PUR-脂肪族+TDI PUR-脂肪族+TDI
填料：
用途：
性能特点：
加工条件：

技术参数

物理性能
PHYSICAL Andur 9000 AP/Curene® 442 Andur 9200 AP/Curene® 442 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D1505

收缩率(MD)
Shrinkage rate % ASTM D955

弹性体
ELASTOMER Andur 9000 AP/Curene® 442 Andur 9200 AP/Curene® 442 单位
UNIT 测试方法
TEST METHOD

压缩形变
Compression deformation % ASTM D395B

巴肖氏弹性
Basho's elasticity % ASTM D2632

拉伸应变(断裂)
Tensile strain % ASTM D412

拉伸强度(100% 应变)
tensile strength MPa

拉伸强度(100% 应变)
tensile strength MPa ASTM D412

拉伸强度(300% 应变)
tensile strength MPa

拉伸强度(300% 应变)
tensile strength MPa ASTM D412

拉伸强度(屈服)
tensile strength MPa ASTM D412

热性能
THERMAL Andur 9000 AP/Curene® 442 Andur 9200 AP/Curene® 442 单位
UNIT 测试方法
TEST METHOD

储存稳定性
storage stability min

后固化时间(96℃)
Post curing time hr

脱模时间
stripping time min

机械性能
MECHANICAL Andur 9000 AP/Curene® 442 Andur 9200 AP/Curene® 442 单位
UNIT 测试方法
TEST METHOD

压缩强度(10% 应变)
compressive strength MPa

压缩强度(10% 应变)
compressive strength MPa ASTM D695

压缩强度(15% 应变)
compressive strength MPa

压缩强度(15% 应变)
compressive strength MPa ASTM D695

压缩强度(25% 应变)
compressive strength MPa

压缩强度(25% 应变)
compressive strength MPa ASTM D695

压缩强度(5% 应变)
compressive strength MPa

压缩强度(5% 应变)
compressive strength MPa ASTM D695

邵氏硬度(邵氏 A)
Shore hardness ASTM D2240

加工方式

注射 Andur 9000 AP/Curene® 442 Andur 9200 AP/Curene® 442 单位测试方法

模具温度 °C

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
弹性体
热性能
机械性能
加工方式
注射
备注
返回顶部

PUR-脂肪族+TDI，Andur 9000 AP/Curene® 442对比PUR-脂肪族+TDI，Andur 9200 AP/Curene® 442对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别