PBT，VALOX™ V2000DM resin对比PBT，VALOX™ HX312C resin物性表,价格行情_搜料

牌号信息	VALOX™ V2000DM resin 物性表 PBT & 沙特沙伯基础指导价格：暂无塑料库存：缺货	VALOX™ HX312C resin 物性表 PBT & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	Valox V2000 dm树脂无筋，直接金属化PBT注射成型树脂，具有高流动性、较好的释放特性。 Unreinforced, directly metallizable PBT injection molding resin with high flow better release characteristics.	带释放装置的无加强PBT。用于医疗设备和医药应用。卫生保健变更管理，生物相容性（ISO 10993或USP六级），符合食品接触。ETO和蒸汽灭菌。 Unreinforced PBT with release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable.

产品描述
厂家：	沙特沙伯基础 SABIC	沙特沙伯基础 SABIC
类别：	PBT polybutylene terephthalate	PBT polybutylene terephthalate
填料：
用途：		药物,医疗/护理用品
性能特点：	流动性高,含脱模剂 High liquidity,Good stripping performance	蒸汽消毒,生物兼容性,食品接触,环氧乙烷消毒 Steam sterilized,Biocompatible,Food contact compliance,Ethylene oxide disinfection
加工条件：	注射成型 Injection Molding	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL VALOX™ V2000DM resin VALOX™ HX312C resin 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate %

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(饱和，23℃)
Water absorption rate %

吸水率(饱和，23℃)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ASTM D792, ISO 1183

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % 内部方法

熔体体积流动速率(250℃，1.2 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体体积流动速率(250℃，2.16 kg)
Melt Volume Rate cm³/10min ISO 1133

熔体质量流动速率(250℃，1.20kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(250℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

机械性能
MECHANICAL VALOX™ V2000DM resin VALOX™ HX312C resin 单位
UNIT 测试方法
TEST METHOD

弯曲强度(--)
bending strength MPa ISO 178

弯曲强度(屈服，50 mm跨度)
bending strength MPa ASTM D790

弯曲模量(--)
Bending modulus MPa ISO 178

弯曲模量(50 mm跨距)
Bending modulus MPa ASTM D790

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(屈服)
Tensile strain % ISO 527-2/50

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2/50

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服)
tensile strength MPa ISO 527-2/50

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2/50

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量(--)
Tensile modulus MPa ASTM D638

拉伸模量(--)
Tensile modulus MPa ISO 527-1-2

冲击性能
IMPACT VALOX™ V2000DM resin VALOX™ HX312C resin 单位
UNIT 测试方法
TEST METHOD

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam

悬臂梁无缺口冲击强度(-30℃)
Notched impact strength of cantilever beam ASTM D4812

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-30℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(-30℃)
Charpy Unnotch Impact strength

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength

简支梁缺口冲击强度(-30℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m²

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Total Energy)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL VALOX™ V2000DM resin VALOX™ HX312C resin 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火，100 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Ae

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火，64 mm跨距)
Hot deformation temperature ℃ ISO 75-2/Af

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(MD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ASTM E831

线性热膨胀系数(TD：-40~40℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(TD：23~80℃)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525 9

维卡软化温度(B120)
Vicat Softening Temp ℃ ISO 306/B120

维卡软化温度(B50)
Vicat Softening Temp ℃ ASTM D1525, ISO 306/B50 10 16

维卡软化温度(B50)
Vicat Softening Temp ℃ ISO 306

加工方式

注射 VALOX™ V2000DM resin VALOX™ HX312C resin 单位测试方法

加工熔体温度 °C

射嘴温度 °C

干燥时间 hr

干燥时间，最大 hr

干燥温度 °C

建议注射量 %

建议的最大水分含量 %

排气孔深度 mm

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 0.20 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 80*10*4 sp=62mm

7 80*10*4

8 80*10*4 mm

9 标准 B (120°C/h), 载荷2 (50N)

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 类型 1, 2.0 in/min

4 0.051 in/min

5 0.079 in/min

6 Yield

7 80*10*4 sp=62mm

8 80*10*4

9 120*10*4 mm

10 标准 B (120°C/h), 载荷2 (50N)


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
加工方式
注射
备注
返回顶部

PBT，VALOX™ V2000DM resin对比PBT，VALOX™ HX312C resin对比物性表,价格行情_搜料_soliao

询价回复情况说明