PPA，LNP™ THERMOCOMP™ UF009S compound对比PPA，Amodel® A-4145 HH物性表,价格行情_搜料

牌号信息	LNP™ THERMOCOMP™ UF009S compound 物性表 PPA & 沙特沙伯基础指导价格：暂无塑料库存：缺货	Amodel® A-4145 HH 物性表 PPA & 比利时索尔维指导价格：暂无塑料库存： 9000kg
牌号简介	LNP ThermocompUF009S是一种基于聚邻苯二甲酰胺树脂的化合物，含有45%的玻璃纤维。这种材料的附加特性包括：热稳定。也称为：lnpThermocomp化合物UF-1009 HS产品再订购名称：UF009S LNP THERMOCOMP UF009S is a compound based on Polyphthalamide resin containing 45% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1009 HS Product reorder name: UF009S	Amodel® A-4145 HH是一种45%玻璃纤维增强的热稳定级聚邻苯二甲酰胺（ppa），其设计目的是在230°C的温度下为热氧化降解提供优异的性能保持。其他特点是快速循环和热水可塑性。本产品特别适用于小尺寸汽车发动机的进气应用，如进气增压空气冷却和废气再循环。黑色：A-4145 HH BK324 Amodel® A-4145 HH is a 45% glass fiber reinforced heat stabilized grade of polyphthalamide (PPA) that has been designed to provide outstanding property retention to thermal oxidative degradation at temperatures of 230°C. Other features are fast cycling and hot water moldability. This product is particularly suitable to air induction applications within downsized automotive engines such as air induction charge air cooling and exhaust gas recirculation. Black: A-4145 HH BK324

产品描述
厂家：	沙特沙伯基础 SABIC	比利时索尔维 Solvay
类别：	PPA PPA	PPA PPA
填料：	玻璃纤维 45	玻璃纤维 45
用途：		金属取代,汽车领域的应用,汽车的发动机罩下的零件
性能特点：	热稳定性好 Heat Stabilized	机械强度好,韧性好,尺寸稳定性好,成型周期快,激光加工-焊接,耐高温,润滑性,耐化学性,低吸湿性,热稳定性好,防火阻燃等级HB Good Rigidity,Good flexibility,Good Dimensional Stability,Quick molding cycle,Laser welding,High Heat Resistance,Lubricating,Solvent resistance,Low moisture absorption,Heat Stabilized,HB
加工条件：	注射成型 Injection Molding	水温模具注塑成型

技术参数

物理性能
PHYSICAL LNP™ THERMOCOMP™ UF009S compound Amodel® A-4145 HH 单位
UNIT 测试方法
TEST METHOD

吸水率(24hr)
Water absorption rate % ASTM D570

吸水率(24hr，50% RH)
Water absorption rate % ASTM D570

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

密度
Density g/cm³ ISO 1183/A

收缩率(MD)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(MD：24 hrs)
Shrinkage rate % ISO 294-4

收缩率(TD)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ASTM D955

收缩率(TD：24 hrs)
Shrinkage rate % ISO 294-4

机械性能
MECHANICAL LNP™ THERMOCOMP™ UF009S compound Amodel® A-4145 HH 单位
UNIT 测试方法
TEST METHOD

剪切强度
shear strength MPa ASTM D732

压缩强度
compressive strength MPa ASTM D695

弯曲强度
bending strength MPa ASTM D790

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ASTM D790

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，200℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，230℃)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度(断裂)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ISO 527-2

拉伸强度(断裂，200℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，230℃)
tensile strength MPa ISO 527-2

拉伸强度(断裂，23℃)
tensile strength MPa ISO 527-2

拉伸模量
Tensile modulus MPa ASTM D638

拉伸模量
Tensile modulus MPa ISO 527-1-2

拉伸模量
Tensile modulus MPa ISO 527-2

泊松比
Poisson's ratio ASTM E132

冲击性能
IMPACT LNP™ THERMOCOMP™ UF009S compound Amodel® A-4145 HH 单位
UNIT 测试方法
TEST METHOD

多轴向仪器化冲击能量
Multi axial instrumented impact energy J ISO 6603-2

悬臂梁无缺口冲击强度(23℃)
Notched impact strength of cantilever beam kJ/m² ISO 180/1U

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D4812

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch kJ/m² ISO 180-1A

简支梁无缺口冲击强度(23℃)
Charpy Unnotch Impact strength kJ/m² ISO 179/1eU

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

装有测量仪表的落镖冲击(23℃，Energy at Peak Load)
Dart impact equipped with measuring instruments J ASTM D3763

热性能
THERMAL LNP™ THERMOCOMP™ UF009S compound Amodel® A-4145 HH 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

热变形温度(1.8 MPa，未退火，3.2 mm)
Hot deformation temperature ℃ ASTM D648

熔融温度
Melting temperature ℃ ASTM D570

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(0 到 100℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(100 到 200℃)
Linear coefficient of thermal expansion cm/cm/℃ ASTM E831

线性热膨胀系数(MD)
Linear coefficient of thermal expansion ASTM E831

线性热膨胀系数(TD)
Linear coefficient of thermal expansion ASTM E831

电气性能
ELECTRICAL LNP™ THERMOCOMP™ UF009S compound Amodel® A-4145 HH 单位
UNIT 测试方法
TEST METHOD

介电常数(1 MHz)
Dielectric constant ASTM D150

介电常数(60 Hz)
Dielectric constant ASTM D150

介电强度(1.6 mm)
Dielectric strength kV/mm ASTM D149

体积电阻率
Volume resistivity ohms·cm ASTM D257

相比漏电起痕指数
Compared to the leakage tracing index V UL 746

耗散因数(1 MHz)
Dissipation factor ASTM D150

耗散因数(60 Hz)
Dissipation factor ASTM D150

高电压电弧起痕速率(HVTR)
High voltage arc marking rate mm/min UL 746

阻燃性能
FLAMMABILITY LNP™ THERMOCOMP™ UF009S compound Amodel® A-4145 HH 单位
UNIT 测试方法
TEST METHOD

阻燃等级(3.20 mm)
Flame retardant level UL 94

加工方式

注射 LNP™ THERMOCOMP™ UF009S compound Amodel® A-4145 HH 单位测试方法

加工熔体温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

螺杆转速 rpm

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

3 80*10*4

1 一般属性：这些不能被视为规格。

2 These flammability ratings are not intended to reflect hazards presented by these or any other materials under actual fire conditions.


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注