HDPE，Polifil® PE RP-HDPE对比HDPE，SABIC® HDPE B5403物性表,价格行情_搜料

牌号信息	Polifil® PE RP-HDPE 物性表 HDPE & 美国TPG 指导价格：暂无塑料库存：缺货	SABIC® HDPE B5403 物性表 HDPE & 沙特沙伯基础指导价格：暂无塑料库存：缺货
牌号简介	POLIFIL RP-HDPE是一种中等硬度的材料，具有良好的韧性。高密度聚乙烯具有优异的耐化学性能和耐环境应力开裂性能。注射成型应用范围从小型容器和盖子到大型板条箱和箱子。使用此信息作为指南，帮助您选择适合您应用的树脂。TPG将为您的应用定制化合物并微调我们的配方。 Polifil ® RP-HDPE is a moderate stiffness material that retains excellent toughness. HDPE exhibits outstanding chemical resistance and environmental stress crack resistance. Injection molding applications range from small containers and lids to large crates and bins. Low melt flow versions are used for blow molded bottles for milk, cosmetics, and chemicals, and in extruded items such as pipes and profiles. High molecular weight (HMW) grades are increasingly used for high strength blown films, and large blow molded items such as drums, water tanks, and toys.	SABIC® HDPE B5403通常用于吹塑未经认证的密封头滚筒，从25升到220升。该产品具有良好的加工性能、抗应力、抗裂性、刚度和冲击性能。本产品不适用于任何医药/医疗应用，也不得用于任何医药/医疗应用。 SABIC® HDPE B5403 is typically used for blow moulding UN certified Tight Head drums, from 25 up to 220 liter. This food approved grade combines good processing performance with good stress crack resistance, stiffness and impact performance. This product is not intended for and must not be used in any pharmaceutical/medical applications.

产品描述
厂家：	美国TPG	沙特沙伯基础 SABIC
类别：	HDPE HDPE	HDPE HDPE
填料：
用途：	装货箱,容器,盖子	鼓
性能特点：	机械强度好,韧性好,耐化学性,抗应力开裂 Good Rigidity,Good flexibility,Solvent resistance,High ESCR	机械强度好,易加工,冲击性能好,食品接触,高密度,抗应力开裂 Good Rigidity,Excellent Processability,High impact resistance,Food contact compliance,High density,High ESCR
加工条件：	注射成型 Injection Molding	吹塑成型

技术参数

物理性能
PHYSICAL Polifil® PE RP-HDPE SABIC® HDPE B5403 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

密度
Density g/cm³ ISO 1183

收缩率(MD：3.2 mm)
Shrinkage rate % ASTM D955

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(190℃，21.6kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率(190℃，5.0kg)
Melt Flow Rate g/10min ISO 1133

冲击性能
IMPACT Polifil® PE RP-HDPE SABIC® HDPE B5403 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(-30℃，模压成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃，模压成型)
Impact strength of cantilever beam notch kJ/m² ISO 180-A

落锤冲击(23℃，12.7 mm)
Drop hammer impact J ASTM D3029

热性能
THERMAL Polifil® PE RP-HDPE SABIC® HDPE B5403 单位
UNIT 测试方法
TEST METHOD

Enthalpy Change
Enthalpy Change J/g ISO 11357-3

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/B

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

熔融温度(DSC)
Melting temperature ℃ ISO 11357-3

维卡软化温度
Vicat Softening Temp ℃ ISO 306/A

机械性能
MECHANICAL Polifil® PE RP-HDPE SABIC® HDPE B5403 单位
UNIT 测试方法
TEST METHOD

弯曲强度(2 mm，模压成型)
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲模量(2 mm，模压成型)
Bending modulus MPa ISO 178

弯曲模量(正切，23℃)
Bending modulus MPa ASTM D790

抗环境应力开裂(Strain Hardening - Gp)
ESCR(Environmental Stress Cracking Resistance) MPa ISO 18488

拉伸应变(屈服，2 mm，模压成型)
Tensile strain % ISO 527-2/1BA/50

拉伸应变(屈服，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，2 mm，模压成型)
Tensile strain % ISO 527-2/1BA/50

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，2 mm，模压成型)
tensile strength MPa ISO 527-2/1BA/50

拉伸强度(断裂，2 mm，模压成型)
tensile strength MPa ISO 527-2/1BA/50

拉伸模量(2 mm，模压成型)
Tensile modulus MPa ISO 527-2/1BA/50

拉伸模量(23℃)
Tensile modulus MPa ASTM D638

邵氏硬度(邵氏 D)
Shore hardness ASTM D1415

邵氏硬度(邵氏 D，模压成型)
Shore hardness ISO 868

备注

1 一般属性：这些不能被视为规格。


相关资讯

牌号简介
产品描述
技术参数
物理性能
冲击性能
热性能
机械性能
加工方式
备注
返回顶部