POM共聚，Kepital® TC3010对比POM共聚，Kepital® F30-52G物性表,价格行情_搜料

牌号信息	Kepital® TC3010 物性表 POM共聚 & 韩国工程指导价格：暂无塑料库存：缺货	Kepital® F30-52G 物性表 POM共聚 & 韩国工程指导价格：暂无塑料库存：缺货
牌号简介	一般注射成型的低粘度等级。用滑石对其进行改性，使其适用于同一应力下比标准级变形量大的零件。显示出良好的尺寸精度。 A low viscosity grade for general injection molding. It was modified with talcum, and so suitable for parts requiring more reducing deformation than that of standard grade under same stress. Exhibits excellent dimensional accuracy.	一种用于一般注射成型的紫外线稳定和光泽降低的低粘度等级。用耐候性和减光物质改性。适用于需要优良耐候性和低光泽特性的应用 Kepital® F30-52G A UV-stabilized and gloss-reduced low-viscosity grade for general injection molding. Modified with a weather-resistant and gloss-reducing substance. Suitable for applications requiring superior weather resistance and low-gloss characteristics Kepital® F30-52G A UV-stabilized and gloss-reduced low-viscosity grade for general injection molding Modified with a weather-resistant and gloss-reducing substance Suitable for applications requiring superior weather resistance and low-gloss characteristics

产品描述
厂家：	韩国工程 Korea Engineering	韩国工程 Korea Engineering
类别：	POM共聚 Copolymer Polyformaldehyde	POM共聚 Copolymer Polyformaldehyde
填料：
用途：	汽车领域的应用,电子数据处理,通用,机器/机械部件,电气元件,凸轮,工业部件,齿轮
性能特点：	低翘曲性,易加工,韧性好,尺寸稳定性好,低粘度,耐疲劳性好,耐磨,耐化学性,热稳定性好,防火阻燃等级HB Low warping,Excellent Processability,Good flexibility,Good Dimensional Stability,Low Viscosity,Fatigue resistance,Good wear resistance,Solvent resistance,Heat Stabilized,HB	耐候抗UV,低光泽,防火阻燃等级HB Weather resistance is good,Low Gloss,HB
加工条件：	注射成型 Injection Molding

技术参数

物理性能
PHYSICAL Kepital® TC3010 Kepital® F30-52G 单位
UNIT 测试方法
TEST METHOD

吸水率(平衡，23℃，50% RH)
Water absorption rate % ISO 62

吸水率(平衡，23℃，60% RH)
Water absorption rate % ASTM D570

密度
Density g/cm³ ISO 1183

密度(--)
Density g/cm³ ASTM D792

密度(--)
Density g/cm³ ISO 1183

收缩率(3.0 mm)
Shrinkage rate % ISO 294-4

收缩率(MD：2.0 mm)
Shrinkage rate % ASTM D955

收缩率(MD：3.0 mm)
Shrinkage rate % 内部方法

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

熔体质量流动速率(190℃，2.16kg)
Melt Flow Rate g/10min ISO 1133

熔体质量流动速率()
Melt Flow Rate g/10min ISO 1133

机械性能
MECHANICAL Kepital® TC3010 Kepital® F30-52G 单位
UNIT 测试方法
TEST METHOD

弯曲强度
bending strength MPa ISO 178

弯曲强度(23℃)
bending strength MPa ASTM D790

弯曲强度(23℃)
bending strength MPa ISO 178

弯曲模量
Bending modulus MPa ISO 178

弯曲模量(23℃)
Bending modulus MPa ASTM D790

弯曲模量(23℃)
Bending modulus MPa ISO 178

拉伸应变(屈服)
Tensile strain % ISO 527-2

拉伸应变(断裂)
Tensile strain % ISO 527-2

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ISO 527-2

拉伸强度
tensile strength MPa ISO 527-2

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ISO 527-2

冲击性能
IMPACT Kepital® TC3010 Kepital® F30-52G 单位
UNIT 测试方法
TEST METHOD

悬臂梁缺口冲击强度(3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

简支梁缺口冲击强度
Charpy Notched Impact Strength kJ/m² ISO 179-1eA

简支梁缺口冲击强度(23℃)
Charpy Notched Impact Strength kJ/m² ISO 179/1eA

热性能
THERMAL Kepital® TC3010 Kepital® F30-52G 单位
UNIT 测试方法
TEST METHOD

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ISO 75-2/A

熔融温度
Melting temperature ℃

熔融温度
Melting temperature ℃ ISO 11357-3

线性热膨胀系数(MD)
Linear coefficient of thermal expansion 1/℃ ISO 11359-2

线性热膨胀系数(MD：20~80℃)
Linear coefficient of thermal expansion 1/℃ ASTM D696

电气性能
ELECTRICAL Kepital® TC3010 Kepital® F30-52G 单位
UNIT 测试方法
TEST METHOD

体积电阻率
Volume resistivity ohms·cm ASTM D257，IEC 60093

体积电阻率
Volume resistivity ohms·cm IEC 60093

表面电阻率
Surface resistivity ohms ASTM D257，IEC 60093

表面电阻率
Surface resistivity ohms IEC 60093

阻燃性能
FLAMMABILITY Kepital® TC3010 Kepital® F30-52G 单位
UNIT 测试方法
TEST METHOD

0.80 mm
0.80 mm UL 94

阻燃等级
Flame retardant level UL 94

加工方式

注射 Kepital® TC3010 Kepital® F30-52G 单位测试方法

射嘴温度 °C

干燥时间 hr

干燥温度 °C

建议的最大水分含量 %

料斗温度 °C

料筒中部温度 °C

料筒前部温度 °C

料筒后部温度 °C

模具温度 °C

背压 MPa

备注

1 一般属性：这些不能被视为规格。

2 100mm diameter


相关资讯

牌号简介
产品描述
技术参数
物理性能
机械性能
冲击性能
热性能
电气性能
阻燃性能
加工方式
注射
备注
返回顶部

POM共聚，Kepital® TC3010对比POM共聚，Kepital® F30-52G对比物性表,价格行情_搜料_soliao

询价回复情况说明

牌号	厂家
类别