PP均聚，TAIRIPRO T8002对比PP均聚，INEOS PP N01G-02物性表,价格行情_搜料

牌号信息	TAIRIPRO T8002 物性表 PP均聚 & 台湾台化指导价格：暂无塑料库存：缺货	INEOS PP N01G-02 物性表 PP均聚 & 瑞士英力士苯领指导价格：暂无塑料库存：缺货
牌号简介	fcfc-pp树脂t8002符合FDA、RoHS和环保证书的要求。 Extrusion CHARACTERISTICS: Excellent impact strength, Excellent resistance to low temp., Brittleness, Good luster	N01G-02是一种低熔融流动速率聚丙烯冲击共聚物，设计用于吹塑、挤压和复合应用。该等级得益于在室温和低温下具有很高的抗冲击性和通用添加剂包装。该材料符合21 CFR 177.1520中规定的美国食品药品管理局的要求。 N01G-02 is a low melt flow rate polypropylene impact copolymer designed for blow molding, extrusion, and compounding applications. The grade benefits from a very high impact resistance at room and low temperatures and a general purpose additive package. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520.

产品描述
厂家：	台湾台化	瑞士英力士苯领 INEOS
类别：	PP均聚 PP homopolymerization	PP均聚 PP homopolymerization
填料：
用途：		复合,吹塑成型应用
性能特点：	抗冲共聚物 Impact copolymer	流动性低,冲击性能好,食品接触,耐低温冲击,抗冲共聚物 Low liquidity,High impact resistance,Food contact compliance,low-temperature impact resistance,Impact copolymer
加工条件：	吹塑成型	吹塑成型

技术参数

物理性能
PHYSICAL TAIRIPRO T8002 INEOS PP N01G-02 单位
UNIT 测试方法
TEST METHOD

密度
Density g/cm³ ASTM D792

收缩率(MD：23℃)
Shrinkage rate % 内部方法

熔体质量流动速率(230℃，2.16kg)
Melt Flow Rate g/10min ASTM D1238

冲击性能
IMPACT TAIRIPRO T8002 INEOS PP N01G-02 单位
UNIT 测试方法
TEST METHOD

Instrumented Impact，Ductility(-20℃)
Instrumented Impact，Ductility ASTM D3763

Instrumented Impact，Ductility(23℃)
Instrumented Impact，Ductility ASTM D3763

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(-20℃)
Impact strength of cantilever beam notch kJ/m² ASTM D256

悬臂梁缺口冲击强度(-20℃，3.2mm)
Impact strength of cantilever beam notch J/m ASTM D256

悬臂梁缺口冲击强度(23℃)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(23℃，3.2mm)
Impact strength of cantilever beam notch ASTM D256

悬臂梁缺口冲击强度(Area)
Impact strength of cantilever beam notch ASTM D256

热性能
THERMAL TAIRIPRO T8002 INEOS PP N01G-02 单位
UNIT 测试方法
TEST METHOD

热变形温度(0.45 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

热变形温度(0.45 MPa，未退火，6.35 mm)
Hot deformation temperature ℃ ASTM D648

热变形温度(1.8 MPa，未退火)
Hot deformation temperature ℃ ASTM D648

维卡软化温度
Vicat Softening Temp ℃ ASTM D1525

机械性能
MECHANICAL TAIRIPRO T8002 INEOS PP N01G-02 单位
UNIT 测试方法
TEST METHOD

弯曲模量(1% 正割)
Bending modulus MPa ASTM D790-A

弯曲模量(23℃)
Bending modulus MPa ASTM D790-A

拉伸应变(屈服)
Tensile strain % ASTM D638

拉伸应变(断裂)
Tensile strain % ASTM D638

拉伸应变(断裂，23℃)
Tensile strain % ASTM D638

拉伸强度(屈服)
tensile strength MPa ASTM D638

拉伸强度(屈服，23℃)
tensile strength MPa ASTM D638

拉伸强度(断裂)
tensile strength MPa ASTM D638

洛氏硬度(R 级)
Rockwell hardness ASTM D785

光学性能
OPTICAL TAIRIPRO T8002 INEOS PP N01G-02 单位
UNIT 测试方法
TEST METHOD

光泽度(60°)
gloss ASTM D2457

加工方式

挤出 TAIRIPRO T8002 INEOS PP N01G-02 单位测试方法

口模温度 °C

备注

1 一般属性：这些不能被视为规格。

2 2.0 in/min

PP均聚，TAIRIPRO T8002对比PP均聚，INEOS PP N01G-02对比物性表,价格行情_搜料_soliao